NiAl Matrix High-Temperature Self-Lubricating Composite

被引：31
|
作者：
Zhu, Shengyu [1 ,2 ]
Bi, Qinling [1 ]
Wu, Hairong [1 ,2 ]
Yang, Jun [1 ]
Liu, Weimin [1 ]
机构：
[1] Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China
[2] Chinese Acad Sci, Grad Univ, Beijing 100039, Peoples R China
来源：
TRIBOLOGY LETTERS | 2011年 / 41卷 / 03期
基金：
中国国家自然科学基金;
关键词：
NiAl matrix; High temperature; Self-lubricating composite; Wear; TRIBOLOGICAL PROPERTIES; SLIDING WEAR; MECHANICAL-PROPERTIES; METALS; PM212; CR;
D O I：
10.1007/s11249-010-9727-9
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
A high-temperature self-lubricating composite NiAl-Cr-Mo-CaF2 was fabricated using the powder metallurgy technique, and the tribological behavior of the composite at a wide range of temperatures (room temperature to 1000 A degrees C) was investigated. The results showed that the composite had a favorable friction coefficient of about 0.2 and an excellent wear resistance of about 1 x 10(-5) mm(3)N(-1)m(-1) at the high temperatures tested (800 and 1000 A degrees C). The excellent self-lubricating performance was attributed to the formation of the glaze film on the worn surface consisting mainly of CaCrO4 and CaMoO4 as high-temperature solid lubricants.
引用
收藏
页码：535 / 540
页数：6
相关论文
共 50 条
  • [21] Microstructure and High-Temperature Wear Performance of FeCr Matrix Self-Lubricating Composites from Room Temperature to 800 °C
    Cui, Gongjun
    Liu, Yanping
    Gao, Guijun
    Liu, Huiqiang
    Kou, Ziming
    MATERIALS, 2020, 13 (01)
  • [22] Effect of Fe on the high-temperature tribological behavior of NiAl/WC-Fex self-lubricating composites produced by thermal explosion
    Liu, Xinying
    Yuan, Jianjun
    Lou, Shumei
    Li, Dongmin
    Cheng, Wenquan
    MATERIALS RESEARCH EXPRESS, 2020, 7 (07)
  • [23] Ni3Al matrix high temperature self-lubricating composites
    Zhu, Shengyu
    Bi, Qinling
    Yang, Jun
    Liu, Weimin
    Xue, Qunji
    TRIBOLOGY INTERNATIONAL, 2011, 44 (04) : 445 - 453
  • [24] High-Temperature Friction and Wear Properties of NiCr/hBN Self-Lubricating Composites
    Zhu, Xuewei
    Wei, Xiaofeng
    Huang, Yuxiang
    Wang, Fu
    Yan, Pengpeng
    METALS, 2019, 9 (03):
  • [25] Improving high-temperature wear resistance of NiCr matrix self-lubricating composites by controlling oxidation and surface texturing
    Xuan Kong
    Wenyao Sun
    Qunchang Wang
    Minghui Chen
    Tao Zhang
    Fuhui Wang
    Journal of Materials Science & Technology, 2022, 131 (36) : 253 - 263
  • [26] Tribological Properties of Ni-based High Temperature Self-Lubricating Composite
    Li Z.
    Zhang Y.
    Zhou J.
    Wang J.
    Chen J.
    Chen, Jianmin (chenjm@lzbac.cn), 2018, Science Press (38): : 161 - 169
  • [27] Application of a high temperature self-lubricating composite coating on steam turbine components
    Wang, WC
    SURFACE & COATINGS TECHNOLOGY, 2004, 177 : 12 - 17
  • [28] Improving high-temperature wear resistance of NiCr matrix self-lubricating composites by controlling oxidation and surface texturing
    Kong, Xuan
    Sun, Wenyao
    Wang, Qunchang
    Chen, Minghui
    Zhang, Tao
    Wang, Fuhui
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2022, 131 : 253 - 263
  • [29] Research progress in preparation and tribological property of ceramic-based high-temperature self-lubricating composite coatings
    Qingshuai, Liu
    Xiubo, Liu
    Yifan, Liu
    Lin, Zhang
    Yuan, Meng
    Huaifei, Liu
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2022, 50 (06): : 61 - 74
  • [30] Self-lubricating composite gear
    不详
    MANUFACTURING ENGINEERING, 1997, 118 (02): : 24 - 24
12345