Damage mechanisms in a short glass fiber reinforced polyamide under fatigue loading

被引：42

作者：

Belmonte, Enrico ^{[1
,2
]}

De Monte, Matthias ^{[2
]}

Hoffmann, Christian-James ^{[2
]}

Quaresimin, Marino ^{[1
]}

机构：

[1] Univ Padua, Dept Management & Engn, Stradella S Nicola 3, I-36100 Vicenza, Italy

[2] Robert Bosch GmbH, Corp Sect Res & Adv Engn Plast Engn, Robert Bosch Campus 1, D-71272 Renningen, Germany

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2017年 / 94卷

关键词：

Short fiber reinforced plastics; Damage mechanisms; Fatigue; Electron microscopy; CRACK-PROPAGATION; POLYMER COMPOSITES; BEHAVIOR; FRACTURE; ORIENTATION; MICROSTRUCTURE; TEMPERATURE; ANISOTROPY; STRENGTH; GROWTH;

D O I：

10.1016/j.ijfatigue.2016.09.008

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This paper presents a damage investigation on a short glass fiber reinforced polyamide (PA66-GF35) under fatigue loading. Plain and notched specimens were tested at room temperature and humidity with load ratio R = 0. Electron microscopy was used to analyze the fracture surface of failed specimens and the crack path of specimens subjected to interrupted fatigue tests. Damage mechanisms were studied investigating the following fractographic features: ductile/brittle matrix fracture behavior, fiber failure/pullout, degree of fibermatrix interfacial adhesion. The aim of the present paper is to understand the nature of damage initiation and propagation in order to lay the foundations for the development of a multi -scale, mechanism-based lifetime prediction model for short fiber reinforced plastics. (C) 2016 Elsevier Ltd. All rights reserved.

引用

页码：145 / 157

页数：13

共 50 条

[21] Damage behavior in multi-stage fatigue testing of glass-fiber-reinforced polyamide 66
Katoh, A
Handa, K
Narisawa, I
POLYMER COMPOSITES, 2004, 25 (01) : 60 - 81
[22] MULTI-SCALE MODELING OF THE FATIGUE BEHAVIOR OF SHORT GLASS FIBER REINFORCED POLYAMIDE NOTCHED SPECIMENS
Belmonte, E.
De Monte, M.
Quaresimin, M.
20TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS, 2015,
[23] Investigation of failure behavior of glass fiber reinforced epoxy laminate under fatigue loading
Gupta, Akash
Singh, Manjeet
WORLD JOURNAL OF ENGINEERING, 2023,
[24] FATIGUE PROCESS IN SHORT CARBON-FIBER-REINFORCED POLYAMIDE 6.6 UNDER ROTATING BENDING AND TORSIONAL FATIGUE
NISITANI, H
NOGUCHI, H
KIM, YH
ENGINEERING FRACTURE MECHANICS, 1993, 45 (04) : 497 - 512
[25] MULTIDIMENSIONAL APPROACH TO EVALUATE THE FATIGUE STRENGTH OF GLASS FIBER REINFORCED POLYAMIDE
Schalk, Thomas
Linnemann, Andreas
PROCEEDINGS OF THE 7TH INTERNATIONAL CONFERENCE ON MECHANICS AND MATERIALS IN DESIGN (M2D2017), 2017, : 597 - 598
[26] Investigation of damage evolution in short glass fibers reinforced polyamide 6,6 under tensile loading using infrared thermography
Ghorbel, A.
Saintier, N.
Dhiab, A.
11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10
[27] Impact fatigue of short glass fiber reinforced polycarbonate
Ho, KC
Hwang, JR
Doong, JL
JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1997, 16 (10) : 903 - 925
[28] Transverse damage in glass fiber reinforced polymer under thermo-mechanical loading
Kraus, David
Trappe, Volker
COMPOSITES PART C: OPEN ACCESS, 2021, 5
[29] Fatigue modeling of short fiber reinforced composites with ductile matrix under cyclic loading
Kabir, M. R.
Lutz, W.
Zhu, K.
Schmauder, S.
COMPUTATIONAL MATERIALS SCIENCE, 2006, 36 (04) : 361 - 366
[30] MECHANISM OF FRACTURE OF SHORT GLASS FIBER-REINFORCED POLYAMIDE THERMOPLASTIC
SATO, N
KURAUCHI, T
SATO, S
KAMIGAITO, O
JOURNAL OF MATERIALS SCIENCE, 1984, 19 (04) : 1145 - 1152

← 1 2 3 4 5 →