PTFE-Modified Mn-Co-Based Catalytic Ceramic Filters with H2O Resistance for Low-Temperature NH3-SCR

被引：8
|
作者：
Li, Kun [1 ]
Zhou, Tao [1 ]
Xu, Xinqiang [1 ]
Han, Changye [1 ]
Zhang, Hua [1 ]
Jin, Jiang [1 ]
机构：
[1] Nanjing Tech Univ, Coll Mat Sci & Engn, Nanjing 211816, Peoples R China
来源：
SUSTAINABILITY | 2022年 / 14卷 / 09期
关键词：
NH3-SCR; catalytic ceramic filter; PTFE-modified; H2O resistance; COMBINED PARTICLE SEPARATION; NO; REDUCTION; REMOVAL; NH3; ENHANCEMENT; MEMBRANE; BEHAVIOR; ELEMENTS; SURFACE;
D O I：
10.3390/su14095353
中图分类号：
X [环境科学、安全科学];
学科分类号：
08 ; 0830 ;
摘要：
Mn-Co-based catalysts were loaded to ceramic filters element by impregnation for the coprocessing of dust and nitrogen oxide (NOx) in flue gas. The influence of the Mn/Co ratio and loading on the catalytic performance was investigated. The Mn-Co-based catalytic ceramic filter with a Mn/Co molar ratio of 2/1 can achieve 99% NO conversion by selective catalytic reduction of NOx with NH3 (NH3-SCR) in the temperature range of 100-180 degrees C, but its resistance to H2O was relatively poor. The filter element was modified by PTFE to improve the H2O resistance. After modification, the catalytic ceramic filter showed superior resistance to H2O and SO2 at low temperatures (100-180 degrees C) and satisfactory self-cleaning performance.
引用
收藏
页数：11
相关论文
共 50 条
  • [41] Effects of synthesis methods on catalytic activities of CoOx–TiO2 for low-temperature NH3-SCR of NO
    Li Zhu
    Yiqing Zeng
    Shule Zhang
    Jinli Deng
    Qin Zhong
    Journal of Environmental Sciences, 2017, (04) : 277 - 287
  • [42] Effects of synthesis methods on catalytic activities of CoOx-TiO2 for low-temperature NH3-SCR of NO
    Zhu, Li
    Zeng, Yiqing
    Zhang, Shule
    Deng, Jinli
    Zhong, Qin
    JOURNAL OF ENVIRONMENTAL SCIENCES, 2017, 54 : 277 - 287
  • [43] Tourmaline-Modified FeMnTiOx Catalysts for Improved Low-Temperature NH3-SCR Performance
    Wang, Fei
    Xie, Zhibo
    Liang, Jinsheng
    Fang, Baizeng
    Piao, Yu'ang
    Hao, Ming
    Wang, Zishuo
    ENVIRONMENTAL SCIENCE & TECHNOLOGY, 2019, 53 (12) : 6989 - 6996
  • [44] V2O5-modified Mn-Ce/AC catalyst with high SO2 tolerance for low-temperature NH3-SCR of NO
    Jiang, Lijun
    Liu, Qingcai
    Ran, Guangjing
    Kong, Ming
    Ren, Shan
    Yang, Jian
    Li, Jiangling
    CHEMICAL ENGINEERING JOURNAL, 2019, 370 (810-821) : 810 - 821
  • [45] Rationally Designed Confined Structure Ce-Mn-TNTs Catalyst for Low-Temperature NH3-SCR Reaction with Superior Activity and H2O/SO2 Tolerance
    Zhao, Qiang
    Huang, Xiaosheng
    Zhao, Tian
    Cui, Rongji
    Zhang, Jiyi
    Tang, Zhicheng
    ACS SUSTAINABLE CHEMISTRY & ENGINEERING, 2024, 12 (26): : 9987 - 10001
  • [46] Unveiling the effect of Al2O3 on PbCl2 resistance over Mn-Ce/AC catalyst for low-temperature NH3-SCR of NO
    Chen, Zhichao
    Wang, Mingming
    Ren, Shan
    Li, Xiaodi
    Chen, Lin
    Li, Jiangling
    Yang, Jian
    Liu, Qingcai
    JOURNAL OF THE TAIWAN INSTITUTE OF CHEMICAL ENGINEERS, 2022, 140
  • [47] Enhanced low-temperature NH3-SCR performance of Ce/TiO2 modified by Ho catalyst
    Zhang, Ting-ting
    Yan, Li-min
    ROYAL SOCIETY OPEN SCIENCE, 2019, 6 (03):
  • [48] Influence of surface active groups on SO2 resistance of birnessite for low-temperature NH3-SCR
    Fang, Xue
    Liu, Yongjun
    Chen, Lingzhu
    Cheng, Yan
    CHEMICAL ENGINEERING JOURNAL, 2020, 399
  • [49] Influence of surface active groups on SO2 resistance of birnessite for low-temperature NH3-SCR
    Fang, Xue
    Liu, Yongjun
    Chen, Lingzhu
    Cheng, Yan
    Chemical Engineering Journal, 2020, 399
  • [50] Mesoporous Mn-Ti amorphous oxides: a robust low-temperature NH3-SCR catalyst
    Yang, Yanran
    Wang, Minghong
    Tao, Zuliang
    Liu, Qing
    Fei, Zhaoyang
    Chen, Xian
    Zhang, Zhuxiu
    Tang, Jihai
    Cui, Mifen
    Qiao, Xu
    CATALYSIS SCIENCE & TECHNOLOGY, 2018, 8 (24) : 6396 - 6406
12345