Small crack growth behavior and life prediction of 7075-T73 forged aluminum alloy

被引：0

作者：

Liu, JZ ^{[1
]}

Wu, XR ^{[1
]}

Ding, CF ^{[1
]}

Romanowski, AL ^{[1
]}

Annigeri, BS ^{[1
]}

Favrow, LH ^{[1
]}

Schneider, GJ ^{[1
]}

Wang, J ^{[1
]}

Smith, SL ^{[1
]}

机构：

[1] Beijing Inst Aeronaut Mat, Beijing 100095, Peoples R China

来源：

FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4 | 1999年

关键词：

D O I：

暂无

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this paper, small-crack growth behavior of 7075-T73 forged aluminum alloy under constant-amplitude (CA) and a block spectrum (BS) loading was investigated experimentally. The results showed that under CA loading, classic small-crack effects were found. The small-crack effects were more pronounced for the negative stress ratio tests. The small-crack effects were not found for the BS loading. The FASTRANII code was used to predict small-crack growth behavior and fatigue lives for single-edge-notch-tension (SENT) specimens under the CA and BS loading and fatigue lives for unnotched specimens under the CA loading. Almost all of the predictions agreed well with the test results. However, the initial defect size used for the unnotched specimen predictions was different from the one used for the SENT specimen predictions. This was discussed and attributed to a size effect.

引用

页码：345 / 352

页数：8

共 50 条

[1] Quantifying spectrum loading effects on fatigue crack growth in 7075-T73 aluminum
Zion, HL
Johnson, WS
Ball, DL
Everett, RA
[J]. JOURNAL OF THE AMERICAN HELICOPTER SOCIETY, 2000, 45 (01) : 11 - 18
[2] The Effects of Anodization Treatment on the Microstructure and Fatigue Behavior of 7075-T73 Aluminum Alloy
Shih, Teng-Shih
Lee, Tin-Hou
Jhou, Ying-Jhe
[J]. MATERIALS TRANSACTIONS, 2014, 55 (08) : 1280 - 1285
[3] Microwaves Furnace Heat Effect on Aluminum Alloy 7075-T73
Aziz, Sadiq Jaffer
Shandookh, Ahmed Adnan
Salman, Rafeef Jumaa
[J]. 2018 INTERNATIONAL CONFERENCE ON ADVANCE IN SUSTAINABLE ENGINEERING AND ITS APPLICATION (ICASEA), 2018, : 238 - 243
[4] Fatigue Crack Nucleation Studies on Sulfuric Acid Anodized 7075-T73 Aluminum
Terence P. Savas
James C. Earthman
[J]. Journal of Materials Engineering and Performance, 2014, 23 : 2131 - 2138
[5] Fatigue Crack Nucleation Studies on Sulfuric Acid Anodized 7075-T73 Aluminum
Savas, Terence P.
Earthman, James C.
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (06) : 2131 - 2138
[6] A study of small crack growth in aluminum alloy 7075-T6
Donnelly, E
Nelson, D
[J]. INTERNATIONAL JOURNAL OF FATIGUE, 2002, 24 (11) : 1175 - 1189
[7] Actual Marine Atmospheric Pre-Corrosion Fatigue Performance of 7075-T73 Aluminum Alloy
Shi, Laixin
Xiang, Lin
Tao, Jianquan
Chen, Qiang
Liu, Jun
Zhong, Yong
[J]. METALS, 2022, 12 (05)
[8] Surface Characterization of 7075-T73 Aluminum Exposed to Anodizing Pretreatment Solutions
Terence P. Savas
James C. Earthman
[J]. Journal of Materials Engineering and Performance, 2008, 17 : 674 - 681
[9] Surface characterization of 7075-T73 aluminum exposed to anodizing pretreatment solutions
Savas, Terence P.
Earthman, James C.
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2008, 17 (05) : 674 - 681
[10] Femtosecond Laser Peening of Friction Stir Welded 7075-T73 Aluminum Alloys
Kawashima, Terumasa
Sano, Tomokazu
Hirose, Akio
Tsutsumi, Seiichiro
Masaki, Kiyotaka
Arakawa, Kazuto
Hori, Hisashi
[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2018, 262 : 111 - 122

← 1 2 3 4 5 →