Contribution of acoustic emission to the understanding of sulfide stress cracking of low alloy steels

被引：37
|
作者：
Smanio, Veronique [2 ,3 ]
Fregonese, Marion [1 ]
Kittel, Jean [2 ]
Cassagne, Thierry [3 ]
Ropital, Francois [2 ]
Normand, Bernard [1 ]
机构：
[1] INSA Lyon, MATEIS UMR5510, F-69621 Villeurbanne, France
[2] IFP Energies Nouvelles, F-69360 Solaize, France
[3] TOTAL, F-64018 Pau, France
来源：
CORROSION SCIENCE | 2011年 / 53卷 / 12期
关键词：
Steel; Hydrogen embrittlement; MONITORING PITTING CORROSION; AUSTENITIC STAINLESS-STEEL; ASSISTED CRACKING; CREVICE CORROSION; INITIATION; ACID;
D O I：
10.1016/j.corsci.2011.07.041
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The acoustic emission technique was applied to standard tests devoted to evaluate sulfide stress cracking susceptibility of steels for oil and gas industry. The mapping of the density of AE signals vs. their location on the specimen gauge length as a function of time allowed early detection of cracking, and gave meaningful information on incubation times and propagation rates. Sulfide stress cracking initiation was correlated with the presence of critical surface defects. A mechanism involving plastic strain and/or metal dissolution was proposed to account for crack propagation. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码：3942 / 3949
页数：8
相关论文
共 50 条
  • [31] EFFECT OF THE MICROSTRUCTURE AND NONMETALLIC INCLUSIONS ON THE SUSCEPTIBILITY OF LOW-ALLOY STEELS TO SULFIDE STRESS-CORROSION CRACKING
    ARTAMOSHKIN, SV
    ASTAFEV, VI
    TETYUEVA, TV
    SOVIET MATERIALS SCIENCE, 1992, 27 (06): : 580 - 585
  • [32] SULFIDE STRESS CORROSION OF SOME MEDIUM AND LOW ALLOY STEELS
    SNAPE, E
    CORROSION, 1967, 23 (06) : 154 - &
  • [33] ACOUSTIC EMISSION DURING STRESS CORROSION CRACKING IN HIGH STRENGTH STEELS.
    McIntyre, P.
    Green, G.
    1978, 20 (03): : 135 - 140
  • [34] ON THE SULFIDE STRESS CRACKING OF LINE PIPE STEELS
    TURN, JC
    WILDE, BE
    TROIANOS, CA
    CORROSION, 1983, 39 (09) : 364 - 370
  • [35] Sulfide Stress Cracking (SSC) of Low Alloy Linepipe Steels in Low H2S Content Sour Environment
    Shimamura, Junji
    Morikawa, Tatsuya
    Yamasaki, Shigeto
    Tanaka, Masaki
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2022, 108 (09): : 642 - 655
  • [36] Sulfide Stress Cracking (SSC) of Low Alloy Linepipe Steels in Low H2S Content Sour Environment
    Shimamura, Junji
    Morikawa, Tatsuya
    Yamasaki, Shigeto
    Tanaka, Masaki
    ISIJ INTERNATIONAL, 2022, 62 (10) : 2095 - 2106
  • [37] EFFECTS OF STRENGTHENING MECHANISMS ON SULFIDE STRESS CRACKING RESISTANCE OF LOW STRENGTH STEELS
    ASAHI, H
    YAGI, A
    UENO, M
    ISIJ INTERNATIONAL, 1993, 33 (11) : 1190 - 1195
  • [38] INTERCRYSTALLINE STRESS-CORROSION CRACKING ON LOW-ALLOY STEELS
    DRODTEN, P
    FORCH, K
    ARCHIV FUR DAS EISENHUTTENWESEN, 1973, 44 (12): : 893 - 898
  • [39] STUDY ON STRESS RELIEF CRACKING IN WELDED LOW-ALLOY STEELS
    ITO, Y
    NAKANISH.M
    SUMITOMO SEARCH, 1972, (07): : 27 - &
  • [40] Effect of Testing Temperature on Sulfide Stress Cracking of Low Alloy Steel
    Kobayashi, Kenji
    Omura, Tomohiko
    Ueda, Masakatsu
    CORROSION, 2018, 74 (06) : 603 - 612