Structure and properties of TiC-TiNi composites alloyed with iron

The structure, composition, and mechanical properties of iron-alloyed TiC-TiNi composite materials are studied. When the titanium carbide framework is sintered with iron and then impregnated with titanium nickelide, iron atoms are found to diffuse into the matrix and form the B2 structure that is inhomogeneous (gradient) in chemical composition and properties and exhibits various temperatures of martensitic transformation. The latter fact shows up in the broadening of the martensitic transformation hysteresis and its shift toward low temperatures with increasing iron content. At room temperature, the strength properties of gradient-matrix TiC-TiNi composites are shown to increase with iron concentration. (C) 2004 MAIK "Nauka / Interperiodica".