Effect of surface flaw on fatigue strength of shot-peened medium-carbon steel

被引：27
|
作者：
Sakamoto, Junji [1 ,2 ]
Lee, Yong-Sung [1 ]
Cheong, Seong-Kyun [1 ]
机构：
[1] Seoul Natl Univ Sci & Technol, Dept Mech & Automot Engn, Seoul 139743, South Korea
[2] Kyushu Univ, Fac Engn, Dept Mech Engn, Fukuoka 8190395, Japan
来源：
ENGINEERING FRACTURE MECHANICS | 2015年 / 133卷
关键词：
Fatigue strength; Shot peening; Surface flaw; Small fatigue crack behavior; Focused ion beam; LIMIT; BEHAVIOR; ALLOY;
D O I：
10.1016/j.engfracmech.2014.11.005
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The effect of surface flaw on fatigue strength of shot-peened medium-carbon steel was experimentally studied. The fatigue crack initiation life, fatigue crack growth life, and fatigue limit in the steel can be increased by using shot peening (SP). The fatigue fracture of SP specimen occurred by the propagations and coalescence of fatigue cracks initiated from the initial cracks due to SP. The fatigue limit of SP specimen was determined by the propagation limit of fatigue crack. When the size of surface flaw is sufficiently small compared to the SP affected zone, the flaws have not significantly changed the fatigue strength of the SP specimens. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：99 / 111
页数：13
相关论文
共 50 条
  • [21] Proposed fatigue damage measurement parameter for shot-peened carbon steel based on fatigue crack growth behavior
    Kim, Jong-Cheon
    Cheong, Seong-Kyun
    Noguchi, Hiroshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2015, 74 : 97 - 106
  • [22] High Cyclic Fatigue Life and Fracture Behaviors of Shot-Peened Bearing Steel
    Yoon, Sang Jae
    Choi, Nak Sam
    TRANSACTIONS OF THE KOREAN SOCIETY OF MECHANICAL ENGINEERS A, 2011, 35 (09) : 1119 - 1129
  • [23] High Cycle Fatigue Behavior of Shot-Peened Steels
    Mirzazadeh, M. M.
    Plumtree, A.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (08): : 2777 - 2784
  • [24] RESIDUAL-STRESS AND FATIGUE OF SHOT-PEENED MATERIALS
    NIKULARI, A
    EXPERIMENTAL MECHANICS, 1982, 22 (05) : N44 - N44
  • [25] Contact fatigue failure analysis of shot-peened gears
    Guagliano, M
    Riva, E
    Guidetti, M
    ENGINEERING FAILURE ANALYSIS, 2002, 9 (02) : 147 - 158
  • [26] Effects of the distribution of multiple surface cracks on fatigue life of a shot-peened specimen
    Ishihara, Sotomi
    Miyao, Kazyu
    Maekawa, Ichiro
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1988, 54 (507): : 1967 - 1973
  • [27] High Cycle Fatigue Behavior of Shot-Peened Steels
    M. M. Mirzazadeh
    A. Plumtree
    Metallurgical and Materials Transactions A, 2012, 43 : 2777 - 2784
  • [28] Experimental Study on Fatigue Behaviour of Shot-Peened Open-Hole Steel Plates
    Wang, Zhi-Yu
    Wang, Qing-Yuan
    Cao, Mengqin
    MATERIALS, 2017, 10 (09):
  • [29] Very high-cycle fatigue behaviour of shot-peened high-carbon-chromium bearing steel
    Shiozawa, K
    Lu, L
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2002, 25 (8-9) : 813 - 822
  • [30] IMPROVEMENT IN BENDING FATIGUE BEHAVIOR OF SHOT-PEENED STEEL 16MNCR5 BY SUBSEQUENT SURFACE TREATMENT
    SCHREIBER, R
    WOHLFAHRT, H
    MACHERAUCH, E
    ARCHIV FUR DAS EISENHUTTENWESEN, 1978, 49 (04): : 207 - 210
12345