Effect of surface flaw on fatigue strength of shot-peened medium-carbon steel

被引：27
|
作者：
Sakamoto, Junji [1 ,2 ]
Lee, Yong-Sung [1 ]
Cheong, Seong-Kyun [1 ]
机构：
[1] Seoul Natl Univ Sci & Technol, Dept Mech & Automot Engn, Seoul 139743, South Korea
[2] Kyushu Univ, Fac Engn, Dept Mech Engn, Fukuoka 8190395, Japan
来源：
ENGINEERING FRACTURE MECHANICS | 2015年 / 133卷
关键词：
Fatigue strength; Shot peening; Surface flaw; Small fatigue crack behavior; Focused ion beam; LIMIT; BEHAVIOR; ALLOY;
D O I：
10.1016/j.engfracmech.2014.11.005
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The effect of surface flaw on fatigue strength of shot-peened medium-carbon steel was experimentally studied. The fatigue crack initiation life, fatigue crack growth life, and fatigue limit in the steel can be increased by using shot peening (SP). The fatigue fracture of SP specimen occurred by the propagations and coalescence of fatigue cracks initiated from the initial cracks due to SP. The fatigue limit of SP specimen was determined by the propagation limit of fatigue crack. When the size of surface flaw is sufficiently small compared to the SP affected zone, the flaws have not significantly changed the fatigue strength of the SP specimens. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：99 / 111
页数：13
相关论文
共 50 条
  • [1] Evolution of residual stress redistribution associated with localized surface microcracking in shot-peened medium-carbon steel during fatigue test
    Kim, Jong-Cheon
    Cheong, Seong-Kyun
    Noguchi, Hiroshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2013, 55 : 147 - 157
  • [2] Description of short fatigue crack growth in a shot-peened medium carbon steel
    Kocanda, D.
    Kocanda, S.
    Tomaszek, H.
    Fatigue and Fracture of Engineering Materials and Structures, 1998, 21 (08): : 977 - 985
  • [3] Description of short fatigue crack growth in a shot-peened medium carbon steel
    Kocanda, D
    Kocanda, S
    Tomaszek, H
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1998, 21 (08) : 977 - 985
  • [4] Effect of surface wear on fretting fatigue strength of shot-peened steels
    Mutoh, Y
    Nishida, T
    Kondoh, K
    Satoh, T
    Yoshii, K
    ENGINEERING AGAINST FATIGUE, 1999, : 633 - 640
  • [5] Fatigue strength of shot-peened welded joints of steel bridges
    Kinoshita, Koji
    Sugawa, Kiyoaki
    Banno, Yuki
    Ono, Yuki
    Yamada, Shohei
    Kameyama, Seiji
    WELDING IN THE WORLD, 2023, 67 (03) : 651 - 668
  • [6] Residual stress relaxation and low- and high-cycle fatigue behavior of shot-peened medium-carbon steel
    Kim, Jong-Cheon
    Cheong, Seong-Kyun
    Noguchi, Hiroshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2013, 56 : 114 - 122
  • [7] Fatigue strength of shot-peened welded joints of steel bridges
    Koji Kinoshita
    Kiyoaki Sugawa
    Yuki Banno
    Yuki Ono
    Shohei Yamada
    Seiji Kameyama
    Welding in the World, 2023, 67 : 651 - 668
  • [8] Fatigue life prediction of shot-peened steel
    Liu, Jinxiang
    Pang, Ming
    INTERNATIONAL JOURNAL OF FATIGUE, 2012, 43 : 134 - 141
  • [9] Fatigue strength prediction methodology of shot-peened materials
    Benkhettab, Mohamed
    Guechichi, Hocine
    Benkabouche, Salah-Eddine
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2019, 104 (9-12): : 4277 - 4287
  • [10] Fatigue strength prediction methodology of shot-peened materials
    Mohamed Benkhettab
    Hocine Guechichi
    Salah-Eddine Benkabouche
    The International Journal of Advanced Manufacturing Technology, 2019, 104 : 4277 - 4287
12345