Oxygen Non-Stoichiometry in Nano-crystalline La0.5Sr0.5CoO3-x Thin Films

被引：2
|
作者：
Wang, S. [1 ]
Cho, S. [2 ]
Wang, H. [2 ]
Jacobson, A. J. [1 ]
机构：
[1] Univ Houston, Dept Chem, Univ Pk, Houston, TX 77204 USA
[2] Texas A&M Univ, Dept Elect Engn, College Stn, TX 77843 USA
来源：
SOLID OXIDE FUEL CELLS 12 (SOFC XII) | 2011年 / 35卷 / 01期
关键词：
ELECTRODES; KINETICS; SOFC;
D O I：
10.1149/1.3570178
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
Nano-crystalline La0.5Sr0.5CoO3-x (LSCO) thin films with a thickness of similar to 400 nm were deposited on a polycrystalline CGO substrate using pulsed laser deposition. AC impedance measurements were performed on symmetric cells between 400-600 degrees C in 0.01 <= pO(2) <= 1 atm. The oxygen non-stoichiometry in LSCO thin films was obtained by utilizing a hypothetical cell where oxygen transport was limited by the surface exchange reaction. It was found that the oxygen non-stoichiometry was about one order of magnitude lower than that observed for bulk LSCO. At 600 degrees C, in air, the area specific resistance (ASR) of the LSCO thin film is about 0.06 ohm cm(2).
引用
收藏
页码：1891 / 1897
页数：7
相关论文
共 50 条
  • [21] Effect of oxygen stoichiometry on the electrical property of thin film La0.5Sr0.5CoO3 prepared by pulsed laser deposition
    Liu, JM
    Ong, CK
    JOURNAL OF APPLIED PHYSICS, 1998, 84 (10) : 5560 - 5565
  • [22] Tuning the ferromagnetic transition temperature in La0.5Sr0.5CoO3 thin films
    Manna, Kaustuv
    Samal, D.
    Elizabeth, Suja
    Kumar, P. S. Anil
    JOURNAL OF APPLIED PHYSICS, 2013, 114 (08)
  • [23] Epitaxial La0.5Sr0.5CoO3 thin films:: Structure, magnetism, and transport
    Torija, M. A.
    Sharma, M.
    Fitzsimmons, M. R.
    Varela, M.
    Leighton, C.
    JOURNAL OF APPLIED PHYSICS, 2008, 104 (02)
  • [24] Vacancy related defects in La0.5Sr0.5CoO3-delta thin films
    Keeble, DJ
    Madhukar, S
    Nielsen, B
    Krishnan, A
    AsokaKumar, P
    Aggarwal, S
    Ramesh, R
    Poindexter, EH
    EPITAXIAL OXIDE THIN FILMS III, 1997, 474 : 229 - 233
  • [25] Properties of La0.5Sr0.5CoO3 thin films grown by laser ablation
    Drozdov, YN
    Klyuenkov, EB
    Salashenko, NN
    Suslov, LA
    INORGANIC MATERIALS, 1997, 33 (06) : 645 - 647
  • [26] Epitaxial La0.5Sr0.5CoO3 thin films: Structure, magnetism, and transport
    Torija, M.A.
    Sharma, M.
    Fitzsimmons, M.R.
    Varela, M.
    Leighton, C.
    Journal of Applied Physics, 2008, 104 (02):
  • [27] Effect of Non-Stoichiometry Oxygen Content on the Magnetization of La1.5Sr0.5NiO4+δ
    P. G. Freeman
    S. R. Giblin
    D. Prabhakaran
    Journal of Superconductivity and Novel Magnetism, 2011, 24 : 1149 - 1152
  • [28] Effect of Non-Stoichiometry Oxygen Content on the Magnetization of La1.5Sr0.5NiO4+δ
    Freeman, P. G.
    Giblin, S. R.
    Prabhakaran, D.
    JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2011, 24 (03) : 1149 - 1152
  • [29] Electrical properties of epitaxial La0.5Sr0.5CoO3 (LSCO) thin films prepared in low oxygen pressure
    Wakiya, N
    Shinozaki, K
    Mizutani, N
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2002, 110 (05) : 353 - 357
  • [30] Lattice mismatch accommodation via oxygen vacancy ordering in epitaxial La0.5Sr0.5CoO3-δ thin films
    Gazquez, J.
    Bose, Shameek
    Sharma, M.
    Torija, M. A.
    Pennycook, S. J.
    Leighton, C.
    Varela, M.
    APL MATERIALS, 2013, 1 (01):
12345