Preparation of Epoxy Sizing Agent for Carbon Fiber by Phase Inversion Emulsification

被引：9
|
作者：
Liu, Jianye [1 ]
Ge, Heyi [1 ]
Chen, Juan [1 ]
Liu, Huashi [1 ]
机构：
[1] Univ Jinan, Sch Mat Sci & Engn, Jinan 250022, Peoples R China
来源：
POLYMERS & POLYMER COMPOSITES | 2012年 / 20卷 / 1-2期
关键词：
COMPOSITES; EMULSION; NANO-SIO2; ADHESION; MATRIX;
D O I：
10.1177/0967391112020001-212
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The epoxy resin and epoxidized polybutadiene were used to prepare the emulsion type epoxy sizing agent for carbon fiber by phase inversion emulsification method. Effects of weight ratio of mixed emulsifiers and emulsifiers/resin (omega(e/r)), shear rate and dripping speed of water on properties of emulsion were investigated by centrifugal sedimentation analysis, particle size analysis and zeta potential measurement. Results showed that the optimal emulsion was obtained when weight ratio of polyoxyethylene nonylphenol phosphoric ammonium (NP-10A) and polyoxyethylene styrenated phenol ether (602) was 2:1, omega(e/r) was 12%, shear rate was 10000 r/min. Conductivity of emulsion by different omega(e/r) was also investigated to represent the variation of conductivity during emulsification process.
引用
收藏
页码：63 / 67
页数：5
相关论文
共 50 条
  • [41] Influence of epoxy sizing of carbon-fiber on the properties of carbon fiber/cyanate ester composites
    Ren, Penggang
    Liang, Guozheng
    Zhang, Zengping
    POLYMER COMPOSITES, 2006, 27 (05) : 591 - 598
  • [42] Remarkable improvement in interfacial shear strength of carbon fiber/epoxy composite by large-scare sizing with epoxy sizing agent containing amine-treated MWCNTs
    Li, Lizhi
    Wang, Jie
    Liu, Wenbo
    Wang, Rongguo
    Yang, Fan
    Hao, Lifeng
    Zheng, Tianlu
    Jiao, Weicheng
    Jiang, Long
    POLYMER COMPOSITES, 2018, 39 (08) : 2734 - 2742
  • [43] A hydrophilic Lignin-Based carbon fiber sizing agent assembled with CNTs towards strengthening epoxy resin
    Liu, Yuhan
    Zhao, Xiaojie
    Zhang, Chenchen
    Liu, Baijun
    Zhang, Huiliang
    Sun, Zhaoyan
    Men, Yongfeng
    Hu, Wei
    Shao, Zhu-Bao
    CHEMICAL ENGINEERING JOURNAL, 2023, 476
  • [44] Improving the interfacial properties of carbon fiber-epoxy resin composites with a graphene-modified sizing agent
    Li, Lingtong
    Yan, Chun
    Xu, Haibing
    Liu, Dong
    Shi, Pengcheng
    Zhu, Yingdan
    Chen, Gang
    Wu, Xiaofei
    Liu, Wenqing
    JOURNAL OF APPLIED POLYMER SCIENCE, 2019, 136 (09)
  • [45] Preparation of crosslinked epoxy microparticles via phase inversion
    Hseih, HK
    Woo, EM
    JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 1996, 34 (15) : 2591 - 2598
  • [46] The preparation and properties of waterborne polyurethane containing epoxy group as paper sizing agent
    Zhao, Yan-Na
    Ji, Ding-Xi
    Gongneng Cailiao/Journal of Functional Materials, 2015, 46 (10): : 10119 - 10122
  • [47] Basalt fiber/epoxy composites improve interfacial adhesion by using epoxy Pickering emulsion sizing agent
    Zhang, Tiantian
    Qiang, Junfeng
    POLYMER ENGINEERING AND SCIENCE, 2025,
  • [48] Polydopamine as sizing on carbon fiber surfaces for enhancement of epoxy laminated composites
    Han, Wei
    Zhang, Hong-Ping
    Tavakoli, Javad
    Campbell, Jonathan
    Tang, Youhong
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2018, 107 : 626 - 632
  • [49] Impact of Epoxy Modified Waterborne Polyurethane Sizing Agent on Interfacial Properties of Carbon Fiber/Cyanate Ester Resin Composite
    Yang J.
    Wu N.
    Pan Y.
    Zhu S.
    Jiao Y.
    Chen L.
    Cailiao Daobao/Materials Reports, 2019, 33 (05): : 1762 - 1767
  • [50] Mechanical improvement of carbon fiber/epoxy composites by sizing functionalized carbon nanotubes on fibers
    Liu, Jiaan
    Yang, Tian
    Wang, Bo
    Yu, Zerun
    Yang, Yanchao
    Sun, Guixun
    POLYMER COMPOSITES, 2024, 45 (12) : 10645 - 10653
12345