Low resistivity transparent indium tin oxide (ITO) films sputtered at room temperature with H2O addition

被引：0
|
作者：
Onisawa, K
Nishimura, E
Ando, M
Satou, T
Takabatake, M
Minemura, T
机构：
来源：
FLAT PANEL DISPLAY MATERIALS II | 1997年 / 424卷
关键词：
D O I：
暂无
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A new kind of amorphous indium tin oxide (ITO) film with good pattern delineation properties and mass production capability, as well as low resistivity and high transparency has been developed. The film was prepared by a cluster-type DC magnetron sputtering apparatus at room temperature with H2O addition to the argon sputtering gas. The amorphous ITO film quality was improved by effective termination of oxygen vacancies with -OH species generated by enhanced decomposition from the added H2O in the plasma.
引用
收藏
页码：341 / 346
页数：4
相关论文
共 50 条
  • [1] Properties of DC magnetron sputtered indium-tin oxide films with the assistance of tiny H2O vapor at low temperature
    Lin, Hui
    Yu, Junsheng
    Lou, Shuangling
    Wang, Jun
    Jiang, Yadong
    ADVANCED OPTICAL MANUFACTURING TECHNOLOGIES, PTS 1 AND 2, 2007, 6722
  • [2] Low-resistivity highly transparent indium-tin-oxide thin films prepared at room temperature by synchrotron radiation ablation
    Akagi, Y
    Hanamoto, K
    Suzuki, H
    Katoh, T
    Sasaki, M
    Imai, S
    Tsudagawa, M
    Nakayama, Y
    Miki, H
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1999, 38 (12A): : 6846 - 6850
  • [3] Studying room temperature RF magnetron-sputtered indium tin oxide (ITO) thin films for large scale applications
    Hossain, M. I.
    Salhi, A.
    Zekri, A.
    Abutaha, A.
    Tong, Y.
    Mansour, S.
    RESULTS IN SURFACES AND INTERFACES, 2025, 18
  • [4] Low temperature deposition of indium tin oxide (ITO) films on plastic substrates
    Singh, V
    Saswat, B
    Kumar, S
    Materials, Integration and Technology for Monolithic Instruments, 2005, 869 : 139 - 144
  • [5] Electrical and optical characterization of indium tin oxide (ITO) films for low resistance transparent electrode
    Yoo, DH
    Shin, MW
    DESIGNING, PROCESSING AND PROPERTIES OF ADVANCED ENGINEERING MATERIALS, PTS 1 AND 2, 2004, 449-4 : 1001 - 1004
  • [6] Surface morphology modelling for the resistivity analysis of low temperature sputtered indium tin oxide thin films on polymer substrates
    Yin, Xuesong
    Tang, Wu
    Weng, Xiaolong
    Deng, Longjiang
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2009, 42 (22)
  • [7] Indium Tin Oxide Films with Low Resistivity at Room Temperature Using DC Magnetron Sputtering with Grid Electrode
    Lee, Ho-Nyun
    Hur, Jin-Young
    Kim, Hyun Jong
    Lee, Min Hyung
    Lee, Hong Kee
    MATERIALS TRANSACTIONS, 2014, 55 (03) : 605 - 609
  • [8] Amorphous to crystalline transition and optoelectronic properties of nanocrystalline indium tin oxide (ITO) films sputtered with high rf power at room temperature
    Malathy, V.
    Sivaranjani, S.
    Vidhya, V. S.
    Prince, J. Joseph
    Balasubramanian, T.
    Sanjeeviraja, C.
    Jayachandran, M.
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2009, 355 (28-30) : 1508 - 1516
  • [9] Properties of dc magnetron sputtered indium tin oxide films on polymeric substrates at room temperature
    Shin, JH
    Shin, SH
    Park, JI
    Kim, HH
    JOURNAL OF APPLIED PHYSICS, 2001, 89 (09) : 5199 - 5203
  • [10] Ferromagnetism in indium tin-oxide (ITO) electrodes at room temperature
    Majumdar, Himadri S.
    Majumdar, Sayani
    Tobjork, Daniel
    Osterbacka, Ronald
    SYNTHETIC METALS, 2010, 160 (3-4) : 303 - 306
12345