Analysis of the microstructure near the crack tip of ASME Gr.92 steel after creep crack growth

被引：29
|
作者：
Sawada, K. [1 ]
Hongo, H. [2 ]
Watanabe, T. [2 ]
Tabuchi, M. [1 ]
机构：
[1] Natl Inst Mat Sci, Mat Reliabil Ctr, Tsukuba, Ibaraki 3050047, Japan
[2] Natl Inst Mat Sci, Mat Data Sheet Stn, Tsukuba, Ibaraki 3050047, Japan
来源：
MATERIALS CHARACTERIZATION | 2010年 / 61卷 / 11期
关键词：
High Cr steel; Creep crack growth; Microstructural change; Stress state; FERRITIC STEELS;
D O I：
10.1016/j.matchar.2010.07.003
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The microstructures near to and remote from the tip of a crack in ASME Gr 92 steel were investigated after creep crack growth at 873 and 898 K focusing on the martensitic lath the dislocation structure and precipitates After creep the mean lath width near the crack hp was obviously larger than that of the virgin material whereas the lath width remote from the crack tip was only slightly larger than that of the virgin material The mean dislocation density near the crack tip markedly decreased after creep whereas only a small change was observed in the dislocation density remote from the crack tip The mean size of M23C6 particles near the crack tip after creep was larger than that of the virgin material whereas their mean size remote from the crack hp was almost the same as that of the virgin material (C) 2010 Elsevier Inc All rights reserved
引用
收藏
页码：1097 / 1102
页数：6
相关论文
共 50 条
  • [21] Effect of creep-fatigue loading condition on crack tip fields of grade 91 steel at crack initiation and growth
    Jung, Hyun-Woo
    Kim, Yun-Jae
    Takahashi, Yukio
    INTERNATIONAL JOURNAL OF FRACTURE, 2021, 231 (01) : 127 - 135
  • [22] Relationship between fatigue crack growth behaviour and local hydrogen concentration near crack tip in pipeline steel
    Dmytrakh, I. M.
    Smiyan, O. D.
    Syrotyuk, A. M.
    Bilyy, O. L.
    INTERNATIONAL JOURNAL OF FATIGUE, 2013, 50 : 26 - 32
  • [23] Analysis of creep crack growth behavior of P92 steel welded joint by experiment and numerical simulation
    Zhao, Lei
    Jing, Hongyang
    Xu, Lianyong
    Han, Yongdian
    Xiu, Junjie
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 558 : 119 - 128
  • [24] CREEP CRACK-GROWTH ASSESSMENT BY MEANS OF A CRACK TIP FAR FIELD CONCEPT
    EWALD, J
    MAILE, K
    TSCHEUSCHNER, R
    NUCLEAR ENGINEERING AND DESIGN, 1989, 117 (02) : 185 - 195
  • [25] Creep, fatigue, and creep-fatigue crack growth behaviours of P92 steel at 600 °C
    Alang, N. A.
    Nikbin, K.
    STRENGTH FRACTURE AND COMPLEXITY, 2022, 15 (01) : 29 - 45
  • [26] Creep crack growth in P92 and P122 alloy steel weldment
    Jeong, CS
    Bae, SY
    Lim, BS
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 446 - 451
  • [27] Ductile crack growth simulation from near crack tip dissipated energy
    Marie, S
    Chapuliot, S
    NUCLEAR ENGINEERING AND DESIGN, 2000, 196 (03) : 293 - 305
  • [28] Numerical simulations of creep damage and crack growth in P92 steel welded joints
    Xu L.
    Wen J.
    Tu S.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (08): : 80 - 88
  • [29] Analysis of crack tip field in materials with creep behavior
    Meng, Qinghua
    Liang, Wenyan
    Wang, Zhenqing
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS XI, 2013, 525-526 : 297 - 300
  • [30] EFFECT OF MICROSTRUCTURE DEGRADATION ON CREEP CRACK-GROWTH
    TVERGAARD, V
    INTERNATIONAL JOURNAL OF FRACTURE, 1990, 42 (02) : 145 - 155
12345