Microstructural Characterisation of Austenitic Heat Resistant Sanicro 25 Steel after Steam Oxidation

被引：2
|
作者：
Rutkowski, Bogdan [1 ]
机构：
[1] AGH Univ Sci & Technol, Fac Met Engn & Ind Comp Sci, Al A Mickiewicza 30, PL-30059 Krakow, Poland
来源：
MATERIALS | 2020年 / 13卷 / 15期
关键词：
steam oxidation; HRSTEM; steel; SEM; PHASE; PRECIPITATION; DISSOLUTION; BEHAVIOR;
D O I：
10.3390/ma13153382
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Microstructural and morphological observations of the surface scale on a high Cr and Ni austenitic heat resistant steel oxidised in water vapour at 700 degrees C are reported. Analysis of microstructure was carried out by analytical techniques of transmission- and scanning electron microscopy. Investigation of M(23)C(6)nucleated at the interface between matrix and the Z-phase precipitates after exposing to high temperature showed semicoherency between M(23)C(6)and the matrix and no coherency with the Z-phase. Plates developed on the oxide scale surface consist of Cr(2)O(3)crystals separated by amorphous SiO2.
引用
收藏
页码：1 / 9
页数：9
相关论文
共 50 条
  • [31] Effect of Silicon on the Steam Oxidation Resistance of a 9%Cr Heat Resistant Steel
    T. Ishitsuka
    Y. Inoue
    H. Ogawa
    Oxidation of Metals, 2004, 61 : 125 - 142
  • [32] Creep Rupture Assessment of New Heat-Resistant Sanicro 25 Steel Using Different Life Prediction Approaches
    Zhao, Lei
    Song, Kai
    Zhang, Yu
    Meng, Shan
    Xu, Lianyong
    Han, Yongdian
    Jing, Hongyang
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (12) : 7464 - 7474
  • [33] Creep Rupture Assessment of New Heat-Resistant Sanicro 25 Steel Using Different Life Prediction Approaches
    Lei Zhao
    Kai Song
    Yu Zhang
    Shan Meng
    Lianyong Xu
    Yongdian Han
    Hongyang Jing
    Journal of Materials Engineering and Performance, 2019, 28 : 7464 - 7474
  • [34] Microstructural stability and oxidation behavior of Sanicro 25 during long-term steam exposure in the temperature range 600-750°C
    Zurek, J.
    Yang, S. -M.
    Lin, D. -Y.
    Huettel, T.
    Singheiser, L.
    Quadakkers, W. J.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2015, 66 (04): : 315 - 327
  • [35] On the origin of extraordinary cyclic strengthening of the austenitic stainless steel Sanicro 25 during fatigue at 700 °C
    Heczko, Milan
    Esser, Bryan D.
    Smith, Timothy M.
    Beran, Premysl
    Mazanova, Veronika
    Kruml, Tomas
    Polak, Jaroslav
    Mills, Michael J.
    JOURNAL OF MATERIALS RESEARCH, 2017, 32 (23) : 4342 - 4353
  • [36] On the origin of extraordinary cyclic strengthening of the austenitic stainless steel Sanicro 25 during fatigue at 700 °C
    Milan Heczko
    Bryan D. Esser
    Timothy M. Smith
    Přemysl Beran
    Veronika Mazánová
    Tomáš Kruml
    Jaroslav Polák
    Michael J. Mills
    Journal of Materials Research, 2017, 32 : 4342 - 4353
  • [37] Effect of Pre-Oxidation on the Steam Oxidation of Heat-Resistant Steel T92
    Xu Hong
    Liang Zhiyuan
    Ding Jianliang
    Zhao Qinxin
    Guan Shipian
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (08) : 733 - 739
  • [38] Field studies of steam oxidation behavior of austenitic heat-resistant steel 10Cr18Ni9Cu3NbN
    Liang, Zhiyuan
    Zhao, Qinxin
    Singh, Preet M.
    Wang, Yungang
    Li, Yuxin
    Wang, Yushu
    ENGINEERING FAILURE ANALYSIS, 2015, 53 : 132 - 137
  • [39] Field studies of steam oxidation behavior of austenitic heat-resistant steel 10Cr18Ni9Cu3NbN
    Liang, Zhiyuan
    Zhao, Qinxin
    Singh, Preet M.
    Wang, Yungang
    Li, Yuxin
    Wang, Yushu
    Engineering Failure Analysis, 2015, 53 : 132 - 137
  • [40] Processing maps and microstructural evolution of the type 347H austenitic heat-resistant stainless steel
    Zhou, Yinghui
    Liu, Yongchang
    Zhou, Xiaosheng
    Liu, Chenxi
    Yu, Liming
    Li, Chong
    Ning, Baoqun
    JOURNAL OF MATERIALS RESEARCH, 2015, 30 (13) : 2090 - 2100
12345