Microstructure features and formation mechanism in a newly developed electroslag welding

Electroslag welding (ESW) is known to show higher heat input than electrogas welding (EGW), resulting in poor low-temperature toughness. However, a newly developed ESW (dev. ESW) method using low-resistivity slag bath exhibited excellent low-temperature toughness as a result of lower effective heat input than conventional EGW, as demonstrated by the faster cooling rates measured in weld metals and estimated using finite element method analyses. This led to much shallower molten pool in the dev. ESW, resulting in much finer columnar grains and thinner centerline axial grains. High cooling speed in the dev. ESW method appeared to contribute to increased acicular ferrite proportion. The uniform microstructure with large acicular ferrite proportion and small number of inclusions in the weld metal permitted the dev. ESW weld metal to possess little variation in Charpy impact energy across the center of weld metal.