Effects of Annealing on the Coercivity in Sintered Nd-Fe-B Magnets

被引：1

作者：

Akiya, Takahiro ^{[1
]}

Kato, Hiroaki ^{[1
,2
]}

Une, Yasuhiro ^{[3
]}

Sagawa, Masato ^{[3
]}

机构：

[1] Tohoku Univ, New Ind Creat Hatchery Ctr, Sendai, Miyagi 9808579, Japan

[2] Yamagata Univ, Grad Sch Sci & Engn, Dept Appl Math & Phys, Yonezawa, Yamagata 9928510, Japan

[3] Intermetallics Co Ltd, Kyoto 6158245, Japan

来源：

JOURNAL OF THE JAPAN INSTITUTE OF METALS | 2012年 / 76卷 / 01期

关键词：

annealing temperature; coercivity; copper small additives; sintered neodymium-iron-boron magnet; post annealing; PERMANENT-MAGNETS; PHASE; MICROSTRUCTURE;

D O I：

10.2320/jinstmet.76.36

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

In order to understand the coercivity enhancement mechanism by annealing in sintered Nd-Fe-B magnets, we performed systematic annealing experiments. It was found that an addition of 0.13% of Cu not only enhance the coercivity but also ease the required cooling condition after annealing to obtain high coercivity. Using single successive annealing technique, we observed a 0.3 MA/m jump in coercivity at annealing temperature T-a=640 degrees C for Cu-free Nd-Fe-B magnets and at T-a=440-460 degrees C for Cu containing ones. We also observed sharp reduction of 0.15 MA/m in coercivity for Cu doped sintered Nd-Fe-B magnets at T-a=600 degrees C. Furthermore, we confirmed a reversible behavior of coercivity at the annealing temperature range which is lower than the optimal annealing temperature. This implies that some kinds of reversible structural natures depending on the temperature are closely related to the coercivity of sintered Nd-Fe-B magnets.

引用

页码：36 / 42

页数：7

共 50 条

[41] Annealing behavior of coercivity in (Nd, Dy)-Fe-B-based sintered magnets
Menushenkov, VP
Savchenko, AG
[J]. PHYSICS OF METALS AND METALLOGRAPHY, 2001, 91 : S249 - S253
[42] Improvement of coercivity in Nd-Fe-B nanocomposite magnets
Saito, Tetsuji
Nozaki, Shunji
Nishio-Hamane, Daisuke
[J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2018, 445 : 49 - 52
[43] Coercivity distributions in Nd-Fe-B sintered magnets produced by the grain boundary diffusion process
Nakamura, H.
Hirota, K.
Ohashi, T.
Minowa, T.
[J]. JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2011, 44 (06)
[44] Design and Fabrication of Sintered Nd-Fe-B Magnets With a Low Temperature Coefficient of Intrinsic Coercivity
Cui, X. G.
Yan, M.
Ma, T. Y.
Luo, W.
Tu, S. J.
[J]. SCIENCE OF SINTERING, 2009, 41 (01) : 91 - 99
[45] Dysprosium Nitride-Modified Sintered Nd-Fe-B Magnets with Increased Coercivity and Resistivity
Liu, Qiongzhen
Zhang, Lanting
Xu, Fang
Dong, Xianping
Wu, Jiansheng
Komuro, Matahiro
[J]. JAPANESE JOURNAL OF APPLIED PHYSICS, 2010, 49 (09)
[46] Evaluation of the Microstructural Contribution to the Coercivity of Fine-Grained Nd-Fe-B Sintered Magnets
Fukada, Togo
Matsuura, Masashi
Goto, Ryota
Tezuka, Nobuki
Sugimoto, Satoshi
Une, Yasuhiro
Sagawa, Masato
[J]. MATERIALS TRANSACTIONS, 2012, 53 (11) : 1967 - 1971
[47] Microstructure evaluation for Dy-free Nd-Fe-B sintered magnets with high coercivity
Goto, R.
Matsuura, M.
Sugimoto, S.
Tezuka, N.
Une, Y.
Sagawa, M.
[J]. JOURNAL OF APPLIED PHYSICS, 2012, 111 (07)
[48] Reutilization of Dy strips in rotating diffusion to enhance coercivity of sintered Nd-Fe-B magnets
Liu, Weiqiang
Chen, Fu
Yue, Ming
Wu, Dan
Gao, Jingyuan
Zhang, Dongtao
Zhang, Hongguo
[J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2018, 465 : 381 - 386
[49] GRAIN-SIZE DEPENDENCE OF COERCIVITY OF SINTERED ND-FE-B PERMANENT-MAGNETS
TANG, WH
ZHOU, SZ
HU, B
[J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1991, 94 (1-2) : 67 - 73
[50] The mechanism of coercivity enhancement by the grain boundary diffusion process of Nd-Fe-B sintered magnets
Sepehri-Amin, H.
Ohkubo, T.
Hono, K.
[J]. ACTA MATERIALIA, 2013, 61 (06) : 1982 - 1990

← 1 2 3 4 5 →