Adhesives and coatings from phenol-formaldehyde/resorcinol-formaldehyde resins

被引：1
|
作者：
Motawie, AM [1 ]
Sadek, EM [1 ]
机构：
[1] Egyptian Petr Res Inst, Petrochem Dept, Cairo, Egypt
来源：
POLYMERS FOR ADVANCED TECHNOLOGIES | 1998年 / 9卷 / 12期
关键词：
adhesives; coatings; resole phenol-formaldehyde resin; resorcinol-formaldehyde resin; activation energy;
D O I：
10.1002/(SICI)1099-1581(199812)9:12<837::AID-PAT842>3.0.CO;2-N
中图分类号：
O63 [高分子化学（高聚物）];
学科分类号：
070305 ; 080501 ; 081704 ;
摘要：
Resale phenal-formaldehyde resins were prepared and modified with the prepared resorcinol-formaldehyde resins. The optimum conditions of formulation and curing processes were studied to obtain modified wood adhesives characterized by high-tensile shear strength values. This study indicated that the more suitable conditions are equal weight ratios of phenol-formaldehyde to resorcinol-formaldehyde resins in the presence of paraformaldehyde (20 or 15wt%) of the resin content as a curing agent at 80 or 25 degrees C for 40 min or 100-110 days, respectively. The activation energies of the curing reactions for phenol-formaldehyde/resorcinol-formaldehyde resin samples were determined. Metallic and glass coatings from the previous pure resins and their formulated cured mixtures were prepared and evaluated as varnishes or paints. (C) 1998 John Wiley & Sons, Ltd.
引用
收藏
页码：837 / 843
页数：7
相关论文
共 50 条
  • [41] On the synthesis and structure of resol phenol-formaldehyde resins
    A. F. Gogotov
    A. A. Varfolomeev
    A. D. Sinegibskaya
    L. V. Kanitskaya
    A. V. Rokhin
    Russian Journal of Applied Chemistry, 2009, 82 : 1102 - 1105
  • [42] PYROLYSIS OF PHENOL-FORMALDEHYDE RESINS .2.
    LEARMONTH, GS
    NABI, LG
    PLASTICS & POLYMERS, 1969, 37 (129): : 209 - +
  • [43] Comparison of the molecular structure between phenol-formaldehyde and phenol-urea-formaldehyde resins
    Du, G.-B. (guanben@swfu.edu.cn), 1600, Editorial Board of Chemistry and Industry of Forest Products, No. 16 Suojin Wucun, Nanjing, 210042, China (33):
  • [44] Plasticity of phenol-formaldehyde resins and molding powders
    Debing, LM
    Silberkraus, SH
    INDUSTRIAL AND ENGINEERING CHEMISTRY, 1941, 33 : 972 - 975
  • [45] CURING OF PHENOL-FORMALDEHYDE RESINS .3.
    GYEVI, EB
    TUDOS, F
    ANGEWANDTE MAKROMOLEKULARE CHEMIE, 1974, 38 (AUG9): : 27 - 33
  • [46] On the synthesis and structure of resol phenol-formaldehyde resins
    Gogotov, A. F.
    Varfolomeev, A. A.
    Sinegibskaya, A. D.
    Kanitskaya, L. V.
    Rokhin, A. V.
    RUSSIAN JOURNAL OF APPLIED CHEMISTRY, 2009, 82 (06) : 1102 - 1105
  • [47] USE OF HYDROXYMETHYLATED LIGNIN IN PHENOL-FORMALDEHYDE RESINS
    Nour-Eddine, El Mansouri
    Yuan Qiaolong
    Huang Farong
    RESEARCH PROGRESS IN PAPER INDUSTRY AND BIOREFINERY (4TH ISETPP), VOLS 1-3, 2010, : 53 - 56
  • [48] AN OCCUPATIONAL DERMATITIS DUE TO PHENOL-FORMALDEHYDE RESINS
    DEJARNAC
    ARCHIVES DES MALADIES PROFESSIONNELLES DE MEDECINE DU TRAVAIL ET DE SECURITE SOCIALE, 1972, 33 (09): : 499 - &
  • [49] Sulfonation of pyropolymeric fibers derived from phenol-formaldehyde resins
    Benak, KR
    Dominguez, L
    Economy, J
    Mangun, CL
    CARBON, 2002, 40 (13) : 2323 - 2332
  • [50] Occupational allergic contact dermatitis from phenol-formaldehyde resins
    Owen, CM
    Beck, MH
    CONTACT DERMATITIS, 2001, 45 (05) : 294 - 295
12345