Influence of sulfur trioxide in clinker on the hydration heat and physical properties of Portland cement

被引：10

作者：

Yamashita, Makio ^{[1
]}

Harada, Takumi ^{[1
]}

Sakai, Etsuo ^{[2
]}

Tsuchiya, Koichi ^{[3
,4
]}

机构：

[1] Cement Co, Cement Res Inst, Mitsubishi Mat Corp, 2270 Yokoze, Yokoze, Saitama 3688504, Japan

[2] Tokyo Inst Technol, Sch Mat & Chem Technol, Meguro Ku, 2-12-1 Ookayama, Tokyo, Japan

[3] Res Ctr Struct Mat, Natl Inst Mat Sci, 1-2-1 Sengen, Tsukuba, Ibaraki 3050047, Japan

[4] Univ Tsukuba, Grad Sch Pure & Appl Sci, 1-1 Tennoudai, Tsukuba, Ibaraki 3055877, Japan

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2020年 / 250卷

关键词：

Cement clinker; SO3; Gypsum; C(3)A; Heat flow; Drying shrinkage; SULFATE; SO3; ALKALI; GYPSUM; REACTIVITY; PHASES; ALITE; FORM;

D O I：

10.1016/j.conbuildmat.2020.118844

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

The cement industry has achieved stable usage of waste gypsum board in clinker production. However, few studies have focused on the heat of hydration and physical properties of cements with high-SO3 clinker with different C(3)A and gypsum contents. Clinker with different amounts of SO3 and coexisting C(3)A was prepared in an electric furnace. Cement samples were then prepared by adding gypsum. Increasing the clinker SO3 content accelerated the alite reaction and caused aluminate hydrate reaction to occur later. Compressive strength at 3 days increased with SO3 content whereas that after 28 days decreased. The drying shrinkage strain of mortar decreased with increasing SO3 content of the clinker and gypsum at each C(3)A content. The decrease of drying shrinkage attributed to SO3 in the clinker was smaller than that caused by gypsum SO3. As the clinker SO3 content increases, cement physical properties can be maintained by adjusting the gypsum content. (C) 2020 Elsevier Ltd. All rights reserved.

引用

页数：10

共 50 条

[31] Influence of altered basalt on the burnability of portland cement clinker
El-Alfi, ESA
INDIAN JOURNAL OF ENGINEERING AND MATERIALS SCIENCES, 2002, 9 (02) : 147 - 152
[32] Effect of selected accelerants on the physical properties of mineral trioxide aggregate and Portland cement
Wiltbank, Kenneth B.
Schwartz, Scott A.
Schindler, William G.
JOURNAL OF ENDODONTICS, 2007, 33 (10) : 1235 - 1238
[33] Influence and Mechanism Research of Hydration Heat Inhibitor on Low-Heat Portland Cement
Jia, Fujie
Yao, Yan
Wang, Jingyu
FRONTIERS IN MATERIALS, 2021, 8
[34] A STUDY OF THE DETERMINATION OF THE HEAT OF HYDRATION OF PORTLAND CEMENT
NEWMAN, ES
JOURNAL OF RESEARCH OF THE NATIONAL BUREAU OF STANDARDS, 1950, 45 (05): : 411 - 417
[35] Influence of alkali sulfates in clinker on the hydration and hardening of Portland cement (vol 180, pg 351, 2018)
Ma, Ying
Qian, Jueshi
CONSTRUCTION AND BUILDING MATERIALS, 2018, 182 : 716 - 716
[36] Heat transfer in the rotary kiln burning Portland cement clinker
Pike, RD
INDUSTRIAL AND ENGINEERING CHEMISTRY, 1929, 21 : 230 - 234
[37] The influence of ethanol-diisopropanolamine on the hydration and mechanical properties of Portland cement
Lu, Xiaolei
Ye, Zhengmao
Zhang, Lina
Hou, Pengkun
Cheng, Xin
CONSTRUCTION AND BUILDING MATERIALS, 2017, 135 : 484 - 489
[38] INFLUENCE OF NATURAL ZEOLITE ON PORTLAND CEMENT HYDRATION PROCESSES AND PROPERTIES OF HARDENED CEMENT PASTE
Kriptavicius, Dalius
Girskas, Giedrius
Skripkiunas, Gintautas
CERAMICS-SILIKATY, 2021, 65 (03) : 247 - 254
[39] Influence of maltodextrin retarder on the hydration kinetics and mechanical properties of Portland cement
Lei, Lei
Li, Ran
Fuddin, Andriana
CEMENT & CONCRETE COMPOSITES, 2020, 114 (114):
[40] Modifying Some Properties of Portland Cement Clinker and Portland Cement by Means of ZnO and ZnS.
Knoefel, D.
1978, 67 (03): : 157 - 161

← 1 2 3 4 5 →