Synthesis of CoFe2O4 nanowire arrays by sol-gel template method

被引：103
|
作者：
Ji, GB [1 ]
Tang, SL
Xu, BL
Gu, BX
Du, YW
机构：
[1] Nanjing Univ, Natl Lab Solid State Microstruct, Nanjing 210093, Peoples R China
[2] Nanjing Univ, Dept Phys, Nanjing 210093, Peoples R China
来源：
CHEMICAL PHYSICS LETTERS | 2003年 / 379卷 / 5-6期
关键词：
D O I：
10.1016/j.cplett.2003.08.090
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
CoFe2O4 nanowire arrays with an average diameter of about 40 nm were prepared in porous anodic aluminum oxide (AAO) template using sol-gel process. Transmission electron microscopy (TEM) diffraction pattern and X-ray diffraction (XRD) showed that the nanowires were polycrystalline phase. Magnetic measurements showed the arrays of nanowires did not show a preferential magnetic orientation, the reason was briefly discussed. The effect of heating rate on the structure and magnetic properties of CoFe2O4 nanowire arrays was investigated. The result showed that the coercivity decreased with the increase of the heating rate. (C) 2003 Elsevier B.V. All rights reserved.
引用
收藏
页码：484 / 489
页数：6
相关论文
共 50 条
  • [31] High coercive field for nanoparticles of CoFe2O4 in amorphous silica sol-gel
    Hutlova, A
    Niznansky, D
    Rehspringer, JL
    Estournès, C
    Kurmoo, M
    ADVANCED MATERIALS, 2003, 15 (19) : 1622 - +
  • [32] dc and high frequency magnetic properties of nanopatterned CoFe2O4 arrays fabricated using sol-gel precursors
    Sheet, Goutam
    Cunliffe, Alexandra R.
    Offerman, Erik J.
    Folkman, Chad M.
    Eom, Chang-Beom
    Chandrasekhar, Venkat
    JOURNAL OF APPLIED PHYSICS, 2010, 107 (10)
  • [33] The sol-gel preparation and AFM study of spinel CoFe2O4 thin film
    Cheng, FX
    Peng, ZY
    Xu, ZG
    Liuao, CS
    Yan, CH
    THIN SOLID FILMS, 1999, 339 (1-2) : 109 - 113
  • [34] Synthesis of the nanocrystalline CoFe2O4 ferrite thin films by a novel sol-gel method using glucose as an additional agent
    Sun, Jianrong
    Wang, Zhiguang
    Wang, Yuyu
    Zhu, Yabin
    Shen, Tielong
    Pang, Lilong
    Wei, Kongfang
    Li, Fashen
    MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2012, 177 (02): : 269 - 273
  • [35] Fabrication and characterization of highly ordered zirconia nanowire arrays by sol-gel template method
    Xu, H
    Qin, DH
    Yang, Z
    Li, HL
    MATERIALS CHEMISTRY AND PHYSICS, 2003, 80 (02) : 524 - 528
  • [36] Preparation and characterization of highly ordered NiO nanowire arrays by sol-gel template method
    Yu, M
    Liu, JH
    Li, SM
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2006, 13 (02): : 169 - 173
  • [37] Preparation and characterization of highly ordered NiO nanowire arrays by sol-gel template method
    Mei Yu
    Journal of University of Science and Technology Beijing(English Edition), 2006, (02) : 169 - 173
  • [38] Fabrication of CoFe2O4 ferrite nanowire arrays in porous silicon template and their local magnetic properties
    郑辉
    韩满贵
    邓龙江
    Chinese Physics B, 2016, 25 (02) : 337 - 341
  • [39] Fabrication of CoFe2O4 ferrite nanowire arrays in porous silicon template and their local magnetic properties
    Zheng, Hui
    Han, Man-Gui
    Deng, Long-Jiang
    CHINESE PHYSICS B, 2016, 25 (02)
  • [40] Sol-gel auto-combustion synthesis of PVP/CoFe2O4 nanocomposite and its magnetic characterization
    Kurtan, U.
    Topkaya, R.
    Baykal, A.
    MATERIALS RESEARCH BULLETIN, 2013, 48 (11) : 4889 - 4895
12345