Microstructural aspect of irradiation assisted stress corrosion cracking of LWR in-core structural materials

被引：2
|
作者：
Kai, JJ [1 ]
Tsai, CH [1 ]
Liu, WJ [1 ]
机构：
[1] Natl Tsing Hua Univ, Dept Engn & Syst Sci, Hsinchu 300, Taiwan
来源：
RADIATION EFFECTS AND DEFECTS IN SOLIDS | 1998年 / 144卷 / 1-4期
关键词：
IASCC; microstructure; irradiation; austenitic stainless steel; RIS; CERT;
D O I：
10.1080/10420159808229675
中图分类号：
TL [原子能技术]; O571 [原子核物理学];
学科分类号：
0827 ; 082701 ;
摘要：
Microstructural evolution of proton-irradiated austenitic stainless steels and Inconel 600 alloy were studied in the temperature range interesting to light water reactor (LWR) core conditions. Radiation-induced solute segregation was observed in all irradiation temperatures at dose of 0.1 dpa and above. Constant extension rate test (CERT) was performed to study the irradiation-assisted stress corrosion cracking (IASCC) behavior of these alloys. Void swelling, dislocation and loop structures, and phase transformation were studied to understand the relationship of microstructural evolution to the IASCC phenomenon. It is found that in low carbon austenitic stainless steels, the gamma --> alpha phase transformation could play an important role in stress corrosion cracking mechanism. Twining dislocations were observed in 304L specimens irradiated at 230 degreesC to 1 dpa.
引用
收藏
页码：171 / 188
页数：18
相关论文
共 50 条
  • [21] Irradiation-Assisted Stress Corrosion Cracking of stainless austenitic steels (IASCC)
    Tanguy, B.
    REVUE DE METALLURGIE-CAHIERS D INFORMATIONS TECHNIQUES, 2011, 108 (01): : 39 - 46
  • [22] Role of slip behavior in the irradiation assisted stress corrosion cracking in austenitic steels
    McMurtrey, M.D.
    Was, G.S.
    15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors 2011, 2011, 2 : 1309 - 1320
  • [23] ROLE OF SLIP BEHAVIOR IN THE IRRADIATION ASSISTED STRESS CORROSION CRACKING IN AUSTENITIC STEELS
    McMurtrey, M. D.
    Was, G. S.
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 1383 - 1394
  • [24] Role of Localized Deformation in Irradiation-Assisted Stress Corrosion Cracking Initiation
    West, Elaine A.
    McMurtrey, Michael D.
    Jiao, Zhijie
    Was, Gary S.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (01): : 136 - 146
  • [25] Role of Localized Deformation in Irradiation-Assisted Stress Corrosion Cracking Initiation
    Elaine A. West
    Michael D. McMurtrey
    Zhijie Jiao
    Gary S. Was
    Metallurgical and Materials Transactions A, 2012, 43 : 136 - 146
  • [26] Irradiation-assisted stress corrosion cracking of austenitic alloys in supercritical water
    Zhou, Rongsheng
    West, Elaine A.
    Jiao, Zhijie
    Was, Gary S.
    JOURNAL OF NUCLEAR MATERIALS, 2009, 395 (1-3) : 11 - 22
  • [27] Role of irradiated microstructure and microchemistry in irradiation-assisted stress corrosion cracking
    Was, GS
    Busby, JT
    PHILOSOPHICAL MAGAZINE, 2005, 85 (4-7) : 443 - 465
  • [28] Probabilistic fracture mechanics of irradiation assisted stress corrosion cracking in stainless steels
    Konstantinovic, M. J.
    21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 3792 - 3798
  • [29] Irradiation-assisted stress corrosion cracking of model austenitic stainless steels
    Chung, HM
    Ruther, WE
    Strain, RV
    Shack, WJ
    Karlsen, TM
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 931 - 939
  • [30] Environmentally Assisted Stress Corrosion Cracking
    Rokkam, Srujan
    Rebak, Raul B.
    Cui, Bai
    Dryepondt, Sebastien
    JOM, 2017, 69 (12) : 2851 - 2852
12345