Low temperature synthesis of MgTa2O6 powders

被引：8
|
作者：
Navale, SC
Samuel, V
Ravi, V [1 ]
机构：
[1] Natl Chem Lab, Phys & Mat Chem Div, Pune 411008, Maharashtra, India
[2] Natl Chem Lab, Catalysis Div, Pune 411008, Maharashtra, India
[3] Natl Chem Lab, Polymer Sci & Engn Div, Pune 411008, Maharashtra, India
来源：
MATERIALS LETTERS | 2005年 / 59卷 / 29-30期
关键词：
ceramics; oxides; X-ray diffraction; electron microscopy; magnesium tantalate;
D O I：
10.1016/j.matlet.2005.07.035
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A combination of digestion and further low temperature calcination to crystallize the product is employed to prepare MgTa2O6 (MT) ceramics. Freshly prepared niobium hydroxide gel is mixed with magnesium hydroxide thoroughly and allowed to react at 100 degrees C under refluxing and stirring conditions for 6-12 h. The X-ray amorphous product so formed is heated at 550 degrees C to form crystalline MgTa2O6. This is the lowest temperature so far reported for the formation of MgTa2O6. For comparison, MT powders were also prepared by the traditional solid state method. Transmission electron microscope (TEM) investigations revealed that the average particle size is 40 nm for the low temperature calcined powders. (C) 2005 Elsevier B.V. All rights reserved.
引用
收藏
页码：3926 / 3928
页数：3
相关论文
共 50 条
  • [41] Synthesis of MnSb2O6 powders through a simple low-temperature method and their test as a gas sensor
    Antonio Casillas-Zamora
    José Trinidad Guillén-Bonilla
    Alex Guillén-Bonilla
    M. Rodríguez-Betancourtt
    Y. L. Casallas-Moreno
    Lorenzo Gildo-Ortiz
    M. de la Luz Olvera‑Amador
    S. A. Tomás
    Héctor Guillén-Bonilla
    Journal of Materials Science: Materials in Electronics, 2020, 31 : 7359 - 7372
  • [42] Low temperature synthesis and characterization of SnTa2O6
    Mizoguchi, Hiroshi
    Sleight, A. W.
    Subramanian, M. A.
    MATERIALS RESEARCH BULLETIN, 2009, 44 (05) : 1022 - 1024
  • [43] LOW-TEMPERATURE SYNTHESIS ROUTE TO MGNB2O6
    HOROWITZ, HS
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1988, 71 (05) : C250 - C251
  • [44] Synthesis and characterization of fine particle ZnFe2O4 powders by a low temperature method
    Li, XY
    Lu, GX
    Li, SB
    JOURNAL OF ALLOYS AND COMPOUNDS, 1996, 235 (02) : 150 - 155
  • [45] Synthesis and characterization of α-Al2O3 nanocrystalline powders by low temperature combustion method
    Li, Wenge
    MULTI-FUNCTIONAL MATERIALS AND STRUCTURES II, PTS 1 AND 2, 2009, 79-82 : 569 - 572
  • [46] Low temperature synthesis and characterization of cubic CaB6 ultrafine powders
    Shi, L
    Gu, YL
    Chen, LY
    Yang, ZC
    Ma, JH
    Qian, YT
    CHEMISTRY LETTERS, 2003, 32 (10) : 958 - 959
  • [47] A LOW TEMPERATURE CALCIOTHERMIC REDUCTION APPROACH FOR THE SYNTHESIS OF LaB6 POWDERS
    Sadhasivam, M.
    Usmaniya, M.
    Berchmans, L. J.
    Sanakaranarayanan, S. R.
    Babu, S. P. Kumaresh
    Vijayaragavan, G.
    ARCHIVES OF METALLURGY AND MATERIALS, 2024, 69 (04) : 1537 - 1541
  • [48] Low temperature synthesis of SrNb2O6 and SrTa2O6 using hydroxide precursor
    Muthurajan, H.
    Kumar, H. H.
    Koteswara Rao, N.
    Pradhan, Sivaram
    Jha, R. K.
    Ravi, V.
    MATERIALS LETTERS, 2008, 62 (6-7) : 892 - 894
  • [49] Hydrothermal synthesis of pollucite (CsAlSi2O6) powders
    MacLaren, I
    Cirre, J
    Ponton, CB
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1999, 82 (11) : 3242 - 3244
  • [50] Low temperature synthesis of γ-LixMnO2 powders in ethylene glycol
    Larcher, D
    Gérand, B
    Tarascon, JM
    INTERNATIONAL JOURNAL OF INORGANIC MATERIALS, 2000, 2 (05): : 389 - 396
12345