Anodic Corrosion Behavior of NiFe2O4-Based Cermet in Na3AlF6-K3AlF6-AlF3 for Aluminum Electrolysis

被引：15
|
作者：
Tian, Zhongliang [1 ]
Lai, Yanqing [1 ]
Yang, Shu [1 ]
Li, Jie [1 ]
Hwang, Jiann-Yang [2 ]
Liu, Yexiang [1 ]
机构：
[1] Cent S Univ, Sch Met & Environm, Changsha 410083, Hunan, Peoples R China
[2] Michigan Technol Univ, Dept Mat Sci & Engn, Houghton, MI 49931 USA
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE | 2015年 / 46卷 / 03期
关键词：
INERT ANODES; NICKEL FERRITE; LOWER TEMPERATURE; SYSTEM; PERFORMANCE; SOLUBILITY;
D O I：
10.1007/s11663-015-0328-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A (Cu,Ni)/(10NiO-NiFe2O4) cermet was tested as an inert anode for aluminum electrolysis in Na3AlF6-K3AlF6-AlF3 melt at 1173 K (900 A degrees C), and its corrosion behavior was studied. The results show that the low-temperature Na3AlF6-K3AlF6-AlF3 bath is beneficial, improving the service conditions. With the combined effects of the electrolyte composition and the nascent oxygen during electrolysis, the metal phase (Cu,Ni) at the surface of anode will not be leached preferentially, but be transferred into the aluminates including FeAl2O4, NiAl2O4 and CuAl2O4. This is helpful for the anode to improve its corrosion resistance.
引用
收藏
页码：1257 / 1261
页数：5
相关论文
共 50 条
  • [1] Anodic Corrosion Behavior of NiFe2O4-Based Cermet in Na3AlF6-K3AlF6-AlF3 for Aluminum Electrolysis
    Zhongliang Tian
    Yanqing Lai
    Shu Yang
    Jie Li
    Jiann-Yang Hwang
    Yexiang Liu
    Metallurgical and Materials Transactions B, 2015, 46 : 1257 - 1261
  • [2] Liquidus Temperatures of System Na3AlF6-K3AlF6-AlF3 for Aluminum Electrolysis at Lower Temperature
    Wei Chen-juan
    Lai Yan-qing
    Li Jie
    Tian Zhong-liang
    Wang Jia-wei
    Zou Zhong
    Liu Ye-xiang
    CHEMICAL RESEARCH IN CHINESE UNIVERSITIES, 2011, 27 (06) : 1019 - 1022
  • [3] Liquidus Temperatures of System Na3AlF6-K3AlF6-AlF3 for Aluminum Electrolysis at Lower Temperature
    WEI Chen-juan
    ChemicalResearchinChineseUniversities, 2011, 27 (06) : 1019 - 1022
  • [4] LIQUIDUS TEMPERATURES OF THE SYSTEM Na3AlF6-K3AlF6-AlF3
    Lai Yanqing
    Xin Pengfei
    Tian Zhongliang
    Wei Chenjuan
    Chen Duan
    Li Jie
    LIGHT METALS 2012, 2012, : 691 - 694
  • [5] SOLUBILITY OF SC2O3 IN NA3ALF6-K3ALF6-ALF3 MELTS
    Tian, Zhongliang
    Hu, Xun
    Lai, Yanqing
    Yang, Shu
    Ye, Shaolong
    Li, Jie
    6TH INTERNATIONAL SYMPOSIUM ON HIGH-TEMPERATURE METALLURGICAL PROCESSING, 2015, : 105 - 112
  • [6] Alumina Solubility in Na3AlF6-K3AlF6-AlF3 Molten Salt System Prospective for Aluminum Electrolysis at Lower Temperature
    LI Jie
    Chemical Research in Chinese Universities, 2012, 28 (01) : 142 - 146
  • [7] Alumina Solubility in Na3AlF6-K3AlF6-AlF3 Molten Salt System Prospective for Aluminum Electrolysis at Lower Temperature
    Li Jie
    Yuan Chang-fu
    Tian Zhong-liang
    Wang Jia-wei
    Lai Yan-qing
    Liu Ye-xiang
    CHEMICAL RESEARCH IN CHINESE UNIVERSITIES, 2012, 28 (01) : 142 - 146
  • [8] CORROSION BEHAVIOR OF CERMET ANODES IN Na3AlF6-K3AlF6-BASED BATHS FOR LOW-TEMPERATURE ALUMINUM ELECTROLYSIS CELLS
    Wang, Guihua
    Sun, Xiaofei
    Wang, Wenshan
    Wang, Deren
    He, Yedong
    TMS2011 SUPPLEMENTAL PROCEEDINGS, VOL 3: GENERAL PAPER SELECTIONS, 2011, : 175 - 182
  • [9] Temperature of primary crystallization in party of system Na3AlF6-K3AlF6-AlF3
    Wang Jiawei
    Lai Yanqing
    Tian Zhongliang
    Li Jie
    Liu Yexiang
    LIGHT METALS 2008, 2008, : 513 - 518
  • [10] Effect of the addition of K3AlF6 into electrolytes on the corrosion behavior of NiFe2O4-based cermet anodes
    Sun, Xiao-Fei
    Wang, Gui-Hua
    Wang, Wen-Shan
    Wang, De-Ren
    He, Ye-Dong
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2010, 32 (12): : 1591 - 1595
12345