Effect of pre-oxidation on the failure mechanisms of EB-PVD thermal barrier coatings with (Ni,Pt)Al bond coats

被引：13
|
作者：
Li, S. [1 ]
Xu, M. M. [1 ]
Zhang, C. Y. [1 ]
Bao, Z. B. [1 ,2 ]
Yang, Y. F. [4 ]
Zhu, S. L. [1 ]
Wang, F. H. [3 ]
机构：
[1] Univ Sci & Technol China, Sch Mat Sci & Engn, Wenhua Rd 72, Shenyang 110016, Peoples R China
[2] Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Wencui Rd 62, Shenyang 110016, Peoples R China
[3] Northeastern Univ, Shenyang Natl Lab Mat Sci, Wenhua Rd 3, Shenyang 110819, Peoples R China
[4] Jinan Univ, Inst Adv Wear & Corros Resistant & Funct Mat, West Huangpu Rd 601, Guangzhou 510632, Peoples R China
来源：
CORROSION SCIENCE | 2021年 / 193卷
基金：
中国国家自然科学基金;
关键词：
Thermal barrier coatings; Platinum; Pre-oxidation; Intermixed zone; Failure mechanism; HIGH-TEMPERATURE; OXIDATION PERFORMANCE; ALUMINA SCALE; GROWN OXIDE; DURABILITY; ALPHA-AL2O3; KINETICS; BEHAVIOR; STRESS;
D O I：
10.1016/j.corsci.2021.109873
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to clarify the effect of pre-oxidation for (Ni,Pt)Al bond coat on failure modes of TBCs, cyclic oxidation behavior of thermal barrier coatings system with both pre-oxidized and normal (Ni,Pt)Al bond coats was investigated at 1100 degrees C. The results indicated that thermal cycling resistance of TBCs was dramatically enhanced by pre-oxidation, where thinner and lower residual stress oxide scale, lighter rumpling of the BC/TGO interface were achieved pre-oxidized. The failure modes of these two TBCs were completely diverse. Besides, the lower oxygen partial pressure effectively enhanced transformation from theta to alpha-Al2O3 during pre-oxidation.
引用
收藏
页数：11
相关论文
共 50 条
  • [11] Thermal shock behavior of EB-PVD thermal barrier coatings based on YSZ ceramic coat and (Ni, Pt)Al metallic bond coat
    Liu, Yuzhuo
    Wang, Xin
    Zhen, Zhen
    Mu, Rende
    He, Limin
    Xu, Zhenhua
    OPEN CERAMICS, 2023, 16
  • [12] Characterization of commercial EB-PVD TBC systems with CVD (Ni,Pt)Al bond coatings
    Haynes, JA
    Lance, MJ
    Pint, BA
    Wright, IG
    SURFACE & COATINGS TECHNOLOGY, 2001, 146 : 140 - 146
  • [13] Erosion of EB-PVD thermal barrier coatings
    Nicholls, JR
    Jaslier, Y
    Rickerby, DS
    MATERIALS AT HIGH TEMPERATURES, 1998, 15 (01) : 15 - 22
  • [14] Oxidation and phase structure of the bond coat in EB-PVD thermal barrier coatings during thermal cycling
    Li, MH
    Sun, XF
    Zhang, ZY
    Gong, SK
    Hu, WY
    Guan, HR
    Hu, ZQ
    ACTA METALLURGICA SINICA, 2002, 38 (01) : 79 - 83
  • [15] Surface geometry and strain energy effects in the failure of a (Ni, Pt)Al/EB-PVD thermal barrier coating
    Vaidyanathan, K
    Jordan, EH
    Gell, M
    ACTA MATERIALIA, 2004, 52 (05) : 1107 - 1115
  • [16] Cyclic behavior of EB-PVD thermal barrier coating systems with modified bond coats
    Schulz, Uwe
    Fritscher, Klaus
    Ebach-Stahl, Andrea
    SURFACE & COATINGS TECHNOLOGY, 2008, 203 (5-7): : 449 - 455
  • [17] Thermal property and failure behavior of LaSmZrO thermal barrier coatings by EB-PVD
    Shen, Zaoyu
    Liu, Guanxi
    Zhang, Rujing
    Dai, Jianwei
    He, Limin
    Mu, Rende
    ISCIENCE, 2022, 25 (04)
  • [18] The erosion of EB-PVD thermal barrier coatings: The competition between mechanisms
    Fleck, N. A.
    Zisis, Th.
    WEAR, 2010, 268 (11-12) : 1214 - 1224
  • [19] Oxidation and damage of EB-PVD thermal barrier coatings under thermal cycling
    Chen, XQ
    Newaz, GM
    JOURNAL OF MATERIALS SCIENCE LETTERS, 2001, 20 (01) : 93 - 95
  • [20] Failure mechanism of EB-PVD thermal barrier coatings on NiAl substrate
    Li He-fei
    Guo Hong-bo
    Gong Sheng-kai
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 (04) : 811 - 815
12345