Corrosion resistance of 13% chromium stainless steel welded joints in flow line applications

被引：0
|
作者：
Ueda, M [1 ]
Amaya, H [1 ]
Hirata, H [1 ]
Kondo, K [1 ]
Murata, Y [1 ]
Komizo, Y [1 ]
机构：
[1] Sumitomo Met Ind Ltd, Corp Res & Dev Labs, Tokyo, Japan
来源：
ADVANCES IN CORROSION CONTROL AND MATERIALS IN OIL AND GAS PRODUCTION | 1999年 / 26期
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The mechanical properties and sulfide stress corrosion (SSC) resistance of weldable surer 13Cr stainless steel welded joints were investigated in flow line application The joints welded by Gas Tungsten Arc (CTA) and Gas Metal Arc (GMA) using matching or over-matching weld metal, consisting of super duplex stainless steel, without any preheating and post weld heal treatment (PWHT), showed strength and toughness and good SSC resistance. However, in the welded joint with the under-matching weld metal that would be adequate for conventional 22Cr duplex stainless steel, SSC occurred near the fusion line. These SSC results could be explained by the stress concentration, obtained by FEM calculation, near the fusion line with the under-matching weld metal. Such stress concentration did not exist in the welded joint with the matching or over-matching weld metal. From these results, the super duplex stainless steel was recommended as a suitable material in the welding of super 13Cr stainless steel pipes.
引用
收藏
页码：267 / 273
页数：7
相关论文
共 50 条
  • [21] Corrosion behavior of hydrogen charged super duplex stainless steel welded joints
    Swierczynska, A.
    Labanowski, J.
    Michalska, J.
    Fydrych, D.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2017, 68 (10): : 1037 - 1045
  • [22] Application of minielectrochemical cell to corrosion studies of welded joints of austenitic stainless steel
    Martin, F.
    Garcia, C.
    Tiedra, P.
    Blanco, Y.
    Lopez, M.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2008, 43 (04) : 343 - 352
  • [23] Metallurgical and corrosion characterization of electron beam welded duplex stainless steel joints
    Singh, Jastej
    Shahi, A. S.
    JOURNAL OF MANUFACTURING PROCESSES, 2020, 50 : 581 - 595
  • [24] Investigation on corrosion under insulation (CUI) of 304 stainless steel welded joints
    Bai, Xiaomin
    Tang, Jianqun
    Gong, Jianming
    Jiang, Yingjie
    FROM FAILURE TO BETTER DESIGN, MANFACTURE AND CONSTRUCTION, 2012, : 389 - 394
  • [25] Contribution to the study of effects of surface state of welded joints in stainless steel upon resistance towards pitting corrosion
    Juraga, I.
    Simunovic, V.
    Spanicek, D.
    METALURGIJA, 2007, 46 (03): : 185 - 189
  • [26] Mechanical properties and corrosion resistance of electron beam offset welded Inconel 718 and 304 stainless steel joints
    Zhao, Junhong
    Chen, Guoqing
    Teng, Xinyan
    Zhang, Lamei
    Yang, Chen
    Leng, Xuesong
    MATERIALS LETTERS, 2025, 391
  • [27] Microstructural analysis and the influence of shot peening on stress corrosion cracking resistance of duplex stainless steel welded joints
    Jebaraj, A. V. (vjebaraj@gmail.com), 1600, National Institute of Science Communication and Information Resources (21):
  • [28] Microstructural analysis and the influence of shot peening on stress corrosion cracking resistance of duplex stainless steel welded joints
    Jebaraj, A. Vinoth
    Ajaykumar, L.
    INDIAN JOURNAL OF ENGINEERING AND MATERIALS SCIENCES, 2014, 21 (02) : 155 - 167
  • [29] Electrochemical studies of welded joints corrosion resistance made from stainless steels
    Kovalev, Mark
    Shakhmatov, Aleksey
    Alhimenko, Aleksey
    MATERIALS TODAY-PROCEEDINGS, 2020, 30 : 501 - 505
  • [30] Study on the Properties of Electron Beam Welded Joints of High Carbon Chromium Stainless Steel
    Dai Y.
    Luo B.
    Fang W.
    Yi Y.
    Hu Y.
    Yi P.
    Cailiao Daobao/Materials Reports, 2023, 37 (17):
12345