Research on Bending and Ballistic Performance of Three-Dimensional Ply-to-Ply Angle Interlock Kevlar/EP Armor Material

The three-dimensional (3D) shallow cross-bending composite material has many advantages in thickness and in-plane direction, such as high strength, high modulus, inter-layer shear strength, as well as large-area area bearing, energy absorption, etc., which has great application potential in the field of bulletproof armor. To prepare a protective material with both excellent bending performance and good ballistic performance, the effects of weft density and layering method on the bending performance and ballistic performance of three-dimensional ply-to-ply angle interlock (3DPPAI) Kevlar/EP armor materials were studied. The results showed that when the weft density of the material was 33 pieces/cm, its bending performance and ballistic resistance were the best. The 3DPPAI Kevlar/EP armor material prepared by orthogonal layup had more advantages in bending performance, and the unidirectional layup had better anti-ballistic performance. The research results will lay the foundation for structural optimization and engineering applications of such materials.