Gelcasting of WC-8wt%Co tungsten cemented carbide

被引：11
|
作者：
Li, Yan [1 ]
Guo, Zhimeng [1 ]
机构：
[1] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
来源：
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2008年 / 26卷 / 05期
关键词：
gelcasting; tungsten cemented carbide; dispersant; monomer; complex shape;
D O I：
10.1016/j.ijrmhm.2007.11.003
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Nonaqueous gelcasting as a novel near-net process has been successfully developed to fabricate large size WC-8wt%Co cemented carbide parts with complex shape. In this paper, the effects of processing parameters such as type of monomers, dispersant and its concentration and solids loading on the theological behavior of WC-8wt%Co slurry based on nonaqueous system were investigated to obtain a flowable and stable suspension with a solids loading as high as possible. Moreover, the properties of green and sintered bodies were also studied. The results showed that the optimum amounts of monomer (HEMA) and dispersant (Solsperse-6000) is 1.71 wt% and 0.3 wt%, respectively, based on the weight of the powder, at which, a maximum solids loading of 52 vol% can be obtained, and the green strength can reach 25 MPa. The transverse rupture strength and hardness of specimens sintered at 1400 degrees C for 2 h achieve 2250 MPa and HRA90, respectively, which are similar to those of specimens made by conventional press/sinter or powder injection molding technology. (C) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码：472 / 477
页数：6
相关论文
共 50 条
  • [21] Effect of ultrasonic-assisted EDM on the surface integrity of cemented tungsten carbide (WC-Co)
    Abdullah, Amir
    Shabgard, Mohammad R.
    Ivanov, A.
    Shervanyi-Tabar, Mohammad T.
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2009, 41 (3-4): : 268 - 280
  • [22] Effect of Microstructural Parameters on the Tensile Property of WC-12∼22wt%Co Cemented Carbide
    Ryu, Seong Hyeon
    Kim, Kyung Il
    Noh, Wooram
    Kim, Sang Sub
    Cho, Gue Serb
    KOREAN JOURNAL OF METALS AND MATERIALS, 2021, 59 (03): : 201 - 208
  • [23] THE INFLUENCE OF CARBIDE GRAIN-SIZE ON THE HOT-HARDNESS OF POLYCRYSTALLINE TUNGSTEN CARBIDE AND WC-CO CEMENTED CARBIDES
    CHATFIELD, C
    POWDER METALLURGY INTERNATIONAL, 1985, 17 (03): : 113 - 115
  • [24] Mechanical properties of WC/Co cemented carbide with larger WC grain size
    Okamoto, S
    Nakazono, Y
    Otsuka, K
    Shimoitani, Y
    Takada, J
    MATERIALS CHARACTERIZATION, 2005, 55 (4-5) : 281 - 287
  • [25] Effects of Co content and WC grain size on wear of WC cemented carbide
    Saito, Hiroyuki
    Iwabuchi, Akira
    Shimizu, Tomoharu
    WEAR, 2006, 261 (02) : 126 - 132
  • [26] Influence of the process temperature of spark plasma sintering on micorsturcture and nanoindentation hardness/Young's modulus of WC-8wt%Co
    Zhang, Jianfeng
    Burkel, Eberhard
    ADVANCED CERAMICS AND NOVEL PROCESSING, 2014, 616 : 56 - 61
  • [27] BONDING PROPERTIES OF TiAlCrSiN COATING / WC-8Co CEMENTED CARBIDE WITH MICROTEXTURED SURFACE
    Gong, Manfeng
    Liu, Guangfa
    Li, Meng
    Xia, Xiaoqun
    Wang, Lei
    Wu, Jianfeng
    Zhang, Shanhua
    Mei, Fang
    ARCHIVES OF METALLURGY AND MATERIALS, 2023, 68 (04) : 1563 - 1570
  • [28] Electrochemical preparation of tungsten, tungsten carbide and cemented tungsten carbide
    Tran-Nguyen, D. -H.
    Jewell, D.
    Fray, D. J.
    TRANSACTIONS OF THE INSTITUTIONS OF MINING AND METALLURGY SECTION C-MINERAL PROCESSING AND EXTRACTIVE METALLURGY, 2014, 123 (01): : 53 - 60
  • [29] BEHAVIOR OF COMPRESSIVE DEFORMATION OF WC-CO CEMENTED CARBIDE
    HARA, A
    IKEDA, T
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1972, 13 (02): : 128 - &
  • [30] Electrochemical separation of tungsten from scrap cemented carbide WC in FLiNaK melt
    Gao, Jie
    Zhang, Liwen
    Li, Guangyue
    Gao, Yun
    Xi, Xiaoli
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2024, 121
12345