Mechanisms of fatigue crack growth in WC-Co cemented carbides

被引：2
|
作者：
Boo, MH [1 ]
Park, CY [1 ]
机构：
[1] KEPRI, Nucl Mech & Mat Grp, Taejon, South Korea
来源：
ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4 | 2005年 / 297-300卷
关键词：
fatigue crack growth; WC-Co; cemented carbides; stress intensity factor; stress ratio; mean free path; phase transformation;
D O I：
10.4028/www.scientific.net/KEM.297-300.1120
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
In order to study the influence of stress ratio and WC grain size, the characteristics of fatigue crack growth were investigated in WC-Co cemented carbides with two different grain sizes of 3 and 6 mu m. Fatigue crack growth tests were carried out over a wide range of fatigue crack growth rates covering the threshold stress intensity factor range AK(th). It was found that crack growth rate da/dN against stress intensity factor range Delta K depended on stress ratio R. The crack growth rate plotted in terms of effective stress intensity factor range Delta K-eff still exhibited the effect of microstructure. Fractographic examination revealed brittle fracture at R=0.1 and ductile fracture at R=0.5 in Co binder phase. The amount of Co phase transformation for stress ratio was closely related to fatigue crack growth characteristics.
引用
收藏
页码：1120 / 1125
页数：6
相关论文
共 50 条
  • [41] Molecular dynamics simulation of graphene deposition and growth on WC-Co cemented carbides
    Ding, Ye-Zhang
    Ye, Yin
    Li, Duo-Sheng
    Xu, Feng
    Lang, Wen-Chang
    Liu, Jun-Hong
    Wen, Xin
    ACTA PHYSICA SINICA, 2023, 72 (06)
  • [42] WC Grain Growth Behavior During Selective Laser Melting of WC-Co Cemented Carbides
    Liu, Jinyang
    Chen, Jian
    Lu, Yang
    Deng, Xin
    Wu, Shanghua
    Lu, Zhongliang
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2023, 36 (06) : 949 - 961
  • [43] Fatigue crack growth of WC-Co cemented carbides: a comparative study using small indentation flaws and long through-thickness cracks
    Mahani, S. Fooladi
    Liu, C.
    Garcia-Marro, F.
    Lin, L. L.
    Cabezas, L.
    Wen, X.
    Mansilla, N.
    Llanes, L.
    INTERNATIONAL JOURNAL OF FRACTURE, 2024, 246 (2-3) : 293 - 307
  • [44] STUDY OF THERMAL FATIGUE CRACK-PROPAGATION IN WC-CO CEMENTED CARBIDE
    LAGERQUIST, M
    POWDER METALLURGY, 1975, 18 (35) : 71 - 88
  • [45] On the Short Surface Fatigue Crack Growth Behavior in a Fine-Grained WC-Co Cemented Carbide
    Mikado, Hiroko
    Ishihara, Sotomi
    Oguma, Noriyasu
    Kawamura, Shingo
    METALS, 2017, 7 (07):
  • [46] Mechanism of the early stages of oxidation of WC-Co cemented carbides
    Chen, Liyong
    Yi, Danqing
    Wang, Bin
    Liu, Huiqun
    Wu, Chunping
    CORROSION SCIENCE, 2016, 103 : 75 - 87
  • [47] Influence of μ-size WC on the Corrosion Behavior of Ultrafine WC/WC-Co Cemented Carbides
    Chao Liu
    Yang Liu
    Yunzhu Ma
    Wensheng Liu
    Yuehui He
    Journal of Superhard Materials, 2019, 41 : 334 - 344
  • [48] Microstructure and properties of WC-Co/CrMnFeCoNi composite cemented carbides
    Dong, Dingqian
    Xiang, Xin
    Huang, Bo
    Xiong, Huiwen
    Zhang, Li
    Shi, Kaihua
    Liao, Jun
    VACUUM, 2020, 179
  • [49] Influence of Ru on the microstructure and performance of WC-Co cemented carbides
    Zeng, Hong
    Liu, Wenbin
    Wei, Chongbin
    Materials Science and Technology (United Kingdom), 2022, 38 (13): : 940 - 946
  • [50] Orientation Distribution of Characteristic Planes in WC-Co Cemented Carbides
    Wang Xilong
    Song Xiaoyan
    Gao Yang
    Liu Xingwei
    Wang Haibin
    Liu Xuemei
    RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (03) : 629 - 634
12345