Superconducting properties of FeSe wires and tapes prepared by a gas diffusion technique

被引：37
|
作者：
Gao, Zhaoshun [1 ]
Qi, Yanpeng [1 ]
Wang, Lei [1 ]
Wang, Dongliang [1 ]
Zhang, Xianping [1 ]
Yao, Chao [1 ]
Ma, Yanwei [1 ]
机构：
[1] Chinese Acad Sci, Key Lab Appl Superconduct, Inst Elect Engn, Beijing 100190, Peoples R China
来源：
SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 2011年 / 24卷 / 06期
基金：
中国国家自然科学基金;
关键词：
D O I：
10.1088/0953-2048/24/6/065022
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Superconducting FeSe in the form of wires and tapes were successfully fabricated using a novel gas diffusion procedure. Structural analysis by means of x-ray diffraction shows that the main phase of tetragonal PbO-type FeSe was obtained by this synthesis method. The zero resistivity transition temperature of the FeSe was confirmed to be 9.3 K. A critical current density as high as 137 A cm(-2) (4 K, self-field) was observed. The results suggest that the diffusion procedure is promising in preparing high-quality FeSe wires and tapes.
引用
收藏
页数：4
相关论文
共 50 条
  • [41] AC loss properties of YBCO superconducting tapes fabricated by IBAD-PLD technique
    Iwakuma, M
    Toyota, K
    Nigo, M
    Kiss, T
    Funaki, K
    Iijima, Y
    Saitoh, T
    Yamada, Y
    Shiohara, Y
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 412 : 983 - 991
  • [42] Spin diffusion in mesoscopic superconducting Al wires
    Shin, YS
    Lee, HJ
    Lee, HW
    Realizing Controllable Quantum States: MESOSCOPIC SUPERCONDUCTIVITY AND SPINTRONICS, 2005, : 383 - 388
  • [43] CRYSTALLOGRAPHIC TEXTURES IN DIFFUSION-PROCESSED SUPERCONDUCTING TAPES
    TOGANO, K
    TACHIKAWA, K
    ROSE, RM
    JOURNAL OF APPLIED PHYSICS, 1978, 49 (10) : 5218 - 5220
  • [44] Analysis of superconducting FeSe thin films deposited by a sputtering technique
    Schneider, R.
    Zaitsev, A. G.
    Fuchs, D.
    Fromknecht, R.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2013, 26 (05):
  • [45] Superconducting joint of Bi-2223/Ag superconducting tapes by diffusion bonding
    Guo Wei
    Zou Guisheng
    Wu Aiping
    Wang Yanjun
    Bai Hailin
    Ren Jialie
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2009, 469 (21): : 1898 - 1901
  • [46] Fabrication of FeSe superconducting tapes with high-energy ball milling aided PIT process
    Feng, Jianqing
    Zhang, Shengnan
    Liu, Jixing
    Li, Chengshan
    Ma, Xiaobo
    Zhang, Pingxiang
    MATERIALS LETTERS, 2016, 170 : 31 - 34
  • [47] Evolution of the superconducting properties in FeSe1-xSx
    Moore, S. A.
    Curtis, J. L.
    Di Giorgio, C.
    Lechner, E.
    Abdel-Hafiez, M.
    Volkova, O. S.
    Vasiliev, A. N.
    Chareev, D. A.
    Karapetrov, G.
    Iavarone, M.
    PHYSICAL REVIEW B, 2015, 92 (23)
  • [48] Investigation of Nb–B Diffusion and the Superconducting Properties of MgB2/Nb/Cu Tapes
    YuYan Sun
    PingXiang Zhang
    QingYang Wang
    Ming Qi
    Fang Yang
    GaoFeng Jiao
    GuoQing Liu
    André Sulpice
    Guo Yan
    Journal of Superconductivity and Novel Magnetism, 2012, 25 : 943 - 950
  • [49] Effect of Nb doping on the microstructure and superconducting properties of FeSe
    Ma, Qingshuang
    Li, Xinhua
    Ma, Zongqing
    Yu, Liming
    Li, Huijun
    SCRIPTA MATERIALIA, 2019, 169 : 65 - 69
  • [50] Improvement of the superconducting properties of polycrystalline FeSe by silver addition
    Nazarova, E.
    Balchev, N.
    Nenkov, K.
    Buchkov, K.
    Kovacheva, D.
    Zahariev, A.
    Fuchs, G.
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2015, 28 (12):
12345