New technique for measurement of rubber-to-metal bond failure

被引：2

作者：

Lawrence, CC ^{[1
]}

Lake, GJ ^{[1
]}

Thomas, AG ^{[1
]}

机构：

[1] Univ E London, Dept Civil Engn, Dagenham, Essex, England

来源：

RUBBER CHEMISTRY AND TECHNOLOGY | 2005年 / 78卷 / 02期

关键词：

D O I：

10.5254/1.3547883

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

A new test. involving combined pure and simple shear, that can produce failure very close to the interface between the rubber and the bonding agent in a rubber-to-metal joint, is described. The test allows changes in the position of the tip of the de-bonded region to be followed with time, enabling the failure rate to be determined. The latter can be related to the strain energy release rate so that a fracture mechanics based analysis can be applied. Failure characteristics can be correlated with features of the de-bond surface. The results suggest that even when failure is very close to the interface. the measured strength is similar to that Of the rubber.

引用

页码：271 / 285

页数：15

共 50 条

[31] TROUBLE SHOOTING RUBBER-TO-METAL BONDING PROBLEMS IN TRANSFER MOLDING
GIBBS, EH
SEBER, JM
ELASTOMERICS, 1984, 116 (04): : 36 - 36
[32] Quality evaluation of rubber-to-metal bonded structures based on shearography
Bin Liu
XingMing Guo
GongJin Qi
DongSheng Zhang
Science China Physics, Mechanics & Astronomy, 2015, 58 : 1 - 8
[33] Rubber-to-metal bonding agents - Challenges of a still young technology
Dehnicke, S.
Zutavern, P.
Krtsch, B.
Gummi, Fasern, Kunststoffe, 2015, 68 (06): : 422 - 427
[34] Insert moulding - automatic manufacturing of rubber-to-metal and rubber-to-plastic moulded components
Arning, M
POLYMERS & POLYMER COMPOSITES, 1997, 5 (08): : 589 - 597
[35] Studying the cure kinetics of rubber-to-metal bonding agents using DMTA
Persson, S
Goude, M
Olsson, T
POLYMER TESTING, 2003, 22 (06) : 671 - 676
[36] TROUBLE-SHOOTING RUBBER-TO-METAL BONDING PROBLEMS IN TRANSFER MOLDING
GIBBS, EH
SEBER, JN
RUBBER CHEMISTRY AND TECHNOLOGY, 1985, 58 (01): : 215 - 215
[37] DEGRADATION OF RUBBER-TO-METAL BONDS DURING SIMULATED CATHODIC DELAMINATION
BOERIO, FJ
HONG, SG
JOURNAL OF ADHESION, 1989, 30 (1-4): : 119 - 134
[38] SEM and XPS testing and analysis of rubber-to-metal bonded parts
Jacks, J
ADHESIVES AGE, 1997, 40 (11): : 36 - 38
[39] Influence of reversion on adhesion in the rubber-to-metal vulcanization-bonding process
Souid, Anouar
Sarda, Alain
Deterre, Remi
Leroy, Eric
POLYMER TESTING, 2015, 41 : 157 - 162
[40] PULL-OUT AND PUSH-OUT TESTS FOR RUBBER-TO-METAL ADHESION
GENT, AN
KAANG, SY
RUBBER CHEMISTRY AND TECHNOLOGY, 1989, 62 (04): : 757 - 766

← 1 2 3 4 5 →