Integrated infrared detectors based on (Ba0.65Sr0.35)TiO3 thin films

被引：0
|
作者：
Wu, Ch. G. [1 ]
Zhang, W. L. [1 ]
Li, Y. R. [1 ]
Liu, X. Zh. [1 ]
Zhu, J. [1 ]
Tao, B. W. [1 ]
机构：
[1] Univ Elect Sci & Technol China, State Key Lab Elect Thin Films & Integrated Devic, Chengdu 610054, Peoples R China
来源：
INTEGRATED FERROELECTRICS | 2007年 / 95卷
关键词：
D O I：
10.1080/10584580701756029
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
The integrated single element infrared detectors were developed for high-loading smart munition application using (Ba0.65Sr0.35)TiO3 (BST) pyroelectric films and SiO2 thermal insulating layer. (Ba,Sr)RuO3 (BSR) seeding-layer was deposited on the Pt/Ti/SiO2/Si to induce BST films c-axis preferred orientation growth. The capacitance dependant with temperature of BST films were measured at the temperature ranging from 230K to 340K, releasing that the temperature coefficient of capacitance was 1.6%/K. The pyroelectric coefficient of BST films was 7.45 x 10(-7) C/K Cm-2 measured by dynamic method. Infrared response evaluation of the fabricated sensor has been carried out with D* of 6.34 x 10(7) cm Hz(1/2)/W indicating that the integrated infrared detectors have potential application as gun-launched smart munition seeker.
引用
收藏
页码：26 / 34
页数：9
相关论文
共 50 条
  • [1] Study on (Ba0.65Sr0.35)TiO3 ferroelectric thin film prepared by RF magnetron sputtering
    Yadian Yu Shengguang, 2007, 1 (62-64+67):
  • [2] Comparison of powder synthesis routes for fabricating (Ba0.65Sr0.35)TiO3 ceramics
    Ali, N. J.
    Milne, S. J.
    JOURNAL OF MATERIALS RESEARCH, 2006, 21 (06) : 1390 - 1398
  • [3] Pt/(Ba0．65Sr0．35)TiO3/Pt漏电流特性研究
    何小祥
    吴传贵
    张万里
    功能材料, 2008, (08) : 1298 - 1301+1305
  • [4] Comparison of powder synthesis routes for fabricating (Ba0.65Sr0.35)TiO3 ceramics
    Ali N.J.
    Milne S.J.
    J Mater Res, 2006, 6 (1390-1398): : 1390 - 1398
  • [5] Leakage current characteristics of (Ba0.65Sr0.35) TiO3thin films with Pt electrodes
    He, Xiao-Xiang
    Wu, Chuan-Gui
    Zhang, Wan-Li
    Gongneng Cailiao/Journal of Functional Materials, 2008, 39 (08): : 1298 - 1301
  • [6] Enhanced Dielectric Properties of Nanocrystalline (Ba0.65Sr0.35)TiO3 Thin Films Grown on CaRuO3 Buffer Layers
    Xiong, H. F.
    Tang, X. G.
    Jiang, L. L.
    Chan, H. L. W.
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2009, 9 (10) : 5834 - 5838
  • [7] Characterization of (Ba0.65Sr0.35)(Ti0.65Zr0.35)O3 thin film
    Byun, JD
    Yoon, JI
    Nahm, S
    Kim, JC
    MATERIALS RESEARCH BULLETIN, 2000, 35 (11) : 1755 - 1761
  • [8] Enhanced field emission of silicon tips coated with sol-gel-derived (Ba0.65Sr0.35)TiO3 thin film
    Chen, XF
    Lu, H
    Zhu, WG
    Tan, OK
    SURFACE & COATINGS TECHNOLOGY, 2005, 198 (1-3): : 266 - 269
  • [9] Dielectric and tunable properties of highly (110)-oriented (Ba0.65Sr0.35)TiO3 thin films deposited on Pt/LaNiO3/SiO2/Si substrates
    Yiping Guo
    Daisuke Akai
    Kazuaki Sawada
    Makoto Ishida
    Mingyuan Gu
    Journal of Sol-Gel Science and Technology, 2009, 49
  • [10] 溶胶-凝胶法制备掺铋(Ba0.65Sr0.35)TiO3薄膜的结晶特性研究
    梁金娥
    方瑜
    肖定全
    朱建国
    四川大学学报(自然科学版), 2005, (自然科学版)
12345