Dissimilar diffusion bonding behavior of hydrogenated Ti2AlNb-based and Ti-6Al-4V alloys

被引:23
|
作者
Zhu, Fuhui [1 ]
Peng, Heli [2 ]
Li, Xifeng [1 ]
Chen, Jun [1 ]
机构
[1] Shanghai Jiao Tong Univ, Dept Plast Technol, Shanghai 200030, Peoples R China
[2] Shanghai Spaceflight Precis Machinery Inst, Shanghai 201600, Peoples R China
基金
中国国家自然科学基金;
关键词
Diffusion bonding; Ti2AlNb-based alloy; Ti-6Al-4V; Hydrogen; Shear strength; ORTHORHOMBIC TITANIUM ALUMINIDE; TIAL-BASED INTERMETALLICS; PERCENT-H ADDITION; MECHANICAL-PROPERTIES; MICROSTRUCTURAL EVOLUTION; TI-55; ALLOY; PHASE-TRANSFORMATIONS; DEFORMATION-BEHAVIOR; TI6AL4V INTERLAYER; SUPERPLASTICITY;
D O I
10.1016/j.matdes.2018.08.034
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effects of hydrogen concentration, heating rate and bonding temperature on dissimilar diffusion bonding of Ti2AlNb-based and Ti-6Al-4V alloys were investigated. The microstructural evolutions of bonded joints and substrates during the diffusion bonding were observed using SEM and EDS while the mechanical properties of the joints were evaluated by shear tests. The average joint shear strength was found dependent on the diffusion zone width determined from EDS line scan. The typical joint interface shows a layered microstructure, comprising Ti2AlNb substrate, continuous beta layer, discontinuous alpha layer, equiaxed beta layer and Ti-6Al-4V substrate. If both substrates are hydrogenated with 0.2 wt% hydrogen before diffusion bonding, a sound joint can be formed at 850 degrees C with a fast heating rate. This sound joint has a shear strength of 711 MPa, and its Ti-6Al-4V substrate favors a non-damaged bimodal microstructure. The fast heating rate also causes less hydrogen desorption and oxidation during the heating stage, which facilitates the subsequent diffusion bonding process. The hydrogen addition influences the diffusion bonding process through three main routes including plasticity improvement, diffusion ability enhancement and microstructure tailoring. (C) 2018 Elsevier Ltd. All rights reserved.
引用
收藏
页码:68 / 78
页数:11
相关论文
共 50 条
  • [41] Interface characteristics in diffusion bonding of a γ-TiAl alloy to Ti-6Al-4V
    Wang, XiuFeng
    Ma, Mo
    Liu, XueBin
    Lin, JianGuo
    JOURNAL OF MATERIALS SCIENCE, 2007, 42 (11) : 4004 - 4008
  • [42] DIFFUSION BONDING OF SIC FIBER REINFORCED TI-6AL-4V ALLOY
    HIROSE, A
    KOTOH, M
    FUKUMOTO, S
    KOBAYASHI, KF
    MATERIALS SCIENCE AND TECHNOLOGY, 1992, 8 (09) : 811 - 815
  • [43] Sinter bonding titanium and Ti-6Al-4V
    Montonera, Darrell
    Nash, Philip
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2018, 96 (5-8): : 2907 - 2914
  • [44] Process and mechanism of chip formation in cutting hydrogenated Ti-6Al-4V alloys
    Li, Hong
    Sun, Zhong-Gang
    Hou, Hong-Liang
    Fu, Yu-Can
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2010, 20 (12): : 2320 - 2326
  • [45] Embrittlement of an Orthorhombic Ti2AlNb-Based Titanium Alloy in a Hydrogenated State
    Senkevich, K. S.
    Umarova, O. Z.
    Zasypkin, V. V.
    RUSSIAN METALLURGY, 2019, 2019 (01): : 31 - 35
  • [46] Embrittlement of an Orthorhombic Ti2AlNb-Based Titanium Alloy in a Hydrogenated State
    K. S. Senkevich
    O. Z. Umarova
    V. V. Zasypkin
    Russian Metallurgy (Metally), 2019, 2019 : 31 - 35
  • [47] Property enhancement of orthorhombic Ti2AlNb-based intermetallic alloys
    Hagiwara, M
    Emura, S
    Araoka, A
    THERMEC'2003, PTS 1-5, 2003, 426-4 : 1715 - 1720
  • [48] The ordering behaviour of the O phase in Ti2AlNb-based alloys
    Wu, B
    Shen, JY
    Chu, MY
    Shang, SL
    Zhang, Z
    Peng, DL
    Liu, SQ
    INTERMETALLICS, 2002, 10 (10) : 979 - 984
  • [49] Microcrack propagation in Ti-6Al-4V alloys
    Hines, JA
    Peters, JO
    Lütjering, G
    FATIGUE BEHAVIOR OF TITANIUM ALLOYS, 1999, : 15 - 22
  • [50] ON THE YOUNG MODULI OF TI-6AL-4V ALLOYS
    FAN, ZY
    SCRIPTA METALLURGICA ET MATERIALIA, 1993, 29 (11): : 1427 - 1432