Crack-healing behavior of Al2O3-TiB2-TiSi2 ceramic material

被引：20
|
作者：
Li, Mingshuang [1 ,2 ]
Huang, Chuanzhen [1 ,2 ]
Zhao, Bin [1 ,2 ]
Liu, Hanlian [1 ,2 ]
Wang, Jun [3 ]
Liu, Zhanqiang [1 ,2 ]
机构：
[1] Shandong Univ, Sch Mech Engn, Ctr Adv Jet Engn Technol CaJET, Jinan 250061, Shandong, Peoples R China
[2] Shandong Univ, Minist Educ, Key Lab High Efficiency & Clean Mech Mfg, Jinan, Shandong, Peoples R China
[3] UNSW, Sch Mech & Mfg Engn, Sydney, NSW 2052, Australia
来源：
CERAMICS INTERNATIONAL | 2018年 / 44卷 / 02期
基金：
中国国家自然科学基金;
关键词：
Crack-healing; Al2O3-TiB2-TiSi2; Strength; Microstructure;
D O I：
10.1016/j.ceramint.2017.10.164
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Al2O3-TiB2-TiSi2 ceramic material was fabricated by vacuum hot pressing technique and the crack healing behavior was investigated by means of high-temperature oxidation. The Vickers hardness indenter was used to precrack with a standard crack length of 300 mu m. According to the recovery of flexural strength and the microstructure of crack appearance, the effects of crack healing temperature, healing time and crack length on crack-healing were studied. At the healing temperature of 800 degrees C for 90 min, the strength of crack-healing specimen was recovered completely and the recovery percentage of flexural strength reached up to 107.25%, compared with the flexural strength of the smooth specimen. The strength of crack-healing specimens with a crack length of 150 mu m and 300 mu m were hilly recovered, but incomplete recovery appeared at the crack length of 500 mu m. The crack-healing mechanism was attributed to the crack-filling with liquid phases of SiO2 and TiO2 obtained by X-ray diffraction. The crack surface of Al2O3-TiB2-TiSi2 ceramic material was observed by Scanning Electron Microscopy and Energy-dispersive Spectrometry.
引用
收藏
页码：2132 / 2137
页数：6
相关论文
共 50 条
  • [31] Strengthening of porous TiB2-SiC ceramics by pre-oxidation and crack-healing
    Zhang, Rubing
    Ye, Changshou
    Zhang, Yaoyao
    APPLIED SURFACE SCIENCE, 2016, 360 : 1036 - 1040
  • [32] ON THE OXIDATION BEHAVIOR OF MONOLITHIC TIB2 AND AL2O3-TIB2 AND SI3N4-TIB2 COMPOSITES
    TAMPIERI, A
    LANDI, E
    BELLOSI, A
    JOURNAL OF THERMAL ANALYSIS, 1992, 38 (12): : 2657 - 2668
  • [33] Effect of TiB2 content on the oxidation behavior of Al2O3/TiB2 composites
    Deng, Jianxin
    Ai, Xing
    Cai Liao Ke Xue Yu Gong/Material Science and Technology, 1996, 4 (02): : 56 - 61
  • [34] Schottky barrier formation at Al/TiB2/TiSi2/Si and Cu/TiB2/TiSi2/Si interfaces
    Pelleg, J
    MICROELECTRONIC ENGINEERING, 2004, 75 (04) : 413 - 422
  • [35] Effects of additives on combustion synthesis of Al2O3-TiB2 ceramic composite
    Wang Deqing
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2009, 29 (08) : 1485 - 1492
  • [36] Friction and wear behaviors of Al2O3-TiB2-SiCw ceramic composite
    Shandong Univ of Technology, Jinan, China
    Mocaxue Xuebao, 3 (289-294):
  • [37] Combustion synthesis of glass (B2O3-Al2O3-MgO)-ceramic (TiB2) composites
    Yi, HC
    Guigne, JY
    Moore, JJ
    Manerbino, AR
    Robinson, LA
    Schowengerdt, FD
    JOURNAL OF MATERIALS SYNTHESIS AND PROCESSING, 2002, 10 (04) : 163 - 174
  • [38] Mechanical properties and microstructure of Al2O3/TiB2 and Al2O3/TiB2/GNPs ceramic tool materials prepared by spark plasma sintering
    Chen, Benshuai
    Xiao, Guangchun
    Yi, Mingdong
    Zhang, Jingjie
    Zhou, Tingting
    Chen, Zhaoqiang
    Xu, Chonghai
    CERAMICS INTERNATIONAL, 2021, 47 (08) : 11748 - 11755
  • [39] Effect of heat treatments on the crack-healing and static fatigue behavior of silicon carbide sintered with Sc2O3 and AlN
    Lee, SK
    Ando, K
    Kim, YW
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2005, 88 (12) : 3478 - 3482
  • [40] Scratching behavior of Al2O3-ZrO2 and Al2O3-ZrO2-SiC ceramic composites
    Kenawy, S. H.
    Mahmoud, M. M.
    AMERICAN CERAMIC SOCIETY BULLETIN, 2007, 86 (07): : 9201 - U13
12345