Thermal cycle fatigue properties of coated and uncoated single crystal superalloy

被引：6
|
作者：
Czech, N [1 ]
Stamm, W [1 ]
机构：
[1] SIEMENS AG, POWER GENERAT GRP KWU, GAS TURBINE BLADING NEW TECHNOL, D-45473 MULHEIM, GERMANY
来源：
SURFACE & COATINGS TECHNOLOGY | 1996年 / 86卷 / 1-3期
关键词：
single crystal; coatings; fatigue properties;
D O I：
10.1016/S0257-8972(96)02947-7
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
In order to increase efficiency and power output of gas turbines, turbine inlet temperatures are being steadily increased. To improve the surface resistance of single crystal (SC) blades against oxidation and corrosion, the base material is coated with MCrAlY type overlay coatings. In addition to the mechanical stresses, the coating are subjected to thermal cycling which can result in fatigue cracking. Thermal cycle fatigue (TCF) properties are an important feature for selection of the system. In this paper we will present a TCF measuring method for a fast screening of uncoated and coated materials. Based on the experience with polycrystalline IN 738 LC and single crystal materials (SC 16) we will discuss TCF data. The cycles to crack initiation of coated SC is strongly influenced by grain boundaries.
引用
收藏
页码：15 / 21
页数：7
相关论文
共 50 条
  • [21] Dissolution of γ' Phase in a Single Crystal Superalloy After High-cycle Fatigue
    Liu Yuan
    Wang Linning
    Yu Jinjiang
    Sun Xiaofeng
    [J]. RARE METAL MATERIALS AND ENGINEERING, 2020, 49 (09) : 2925 - 2929
  • [22] Dissolution of γ' Phase in a Single Crystal Superalloy After High-cycle Fatigue
    一种镍基单晶高温合金高周疲劳引起的γ'溶解行为
    [J]. Wang, Linning (lnwang00@163.com), 1600, Science Press (49): : 2925 - 2929
  • [23] Effect of Stress Ratio on High Cycle Fatigue Behavior of a Single Crystal Superalloy
    Xie, Hongji
    Li, Jiarong
    Han, Mei
    [J]. Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2018, 47 (11): : 3381 - 3386
  • [24] High cycle fatigue in a single crystal superalloy: Time dependence at elevated temperature
    Wright, PK
    Jain, M
    Cameron, D
    [J]. Superalloys 2004, 2004, : 657 - 666
  • [25] Influence of surface recrystallization on the low cycle fatigue behaviour of a single crystal superalloy
    Ma, X.
    Shi, H. -J.
    Gu, J.
    Yang, Z.
    Chen, G.
    Luesebrink, O.
    Harders, H.
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2015, 38 (03) : 340 - 351
  • [26] Low cycle fatigue modeling for nickel-based single crystal superalloy
    Tang, Haibin
    Guo, Haiding
    [J]. MATERIALS AT HIGH TEMPERATURES, 2018, 35 (06) : 535 - 545
  • [27] Effect of Stress Ratio on High Cycle Fatigue Behavior of a Single Crystal Superalloy
    Xie Hongji
    Li Jiarong
    Han Mei
    [J]. RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (11) : 3381 - 3386
  • [28] Micromechanics of failure of aluminide coated single crystal Ni superalloy under thermomechanical fatigue
    Zhang, YH
    Knowles, DM
    Withers, PJ
    [J]. SCRIPTA MATERIALIA, 1997, 37 (06) : 815 - 820
  • [29] Isothermal fatigue of an aluminide-coated single-crystal superalloy .1.
    Totemeier, TC
    King, JE
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (02): : 353 - 361
  • [30] Crack initiation and propagation around holes of Ni-based single crystal superalloy during thermal fatigue cycle
    Wang, Li
    Zhou, Zhongjiao
    Zhang, Shaohua
    Jiang, Xiangdong
    Lou, Langhong
    Zhang, Jian
    [J]. Jinshu Xuebao/Acta Metallurgica Sinica, 2015, 51 (10): : 1273 - 1278
12345