Production of Ductile Iron Castings with Different Matrix Structure

被引：0

作者：

Bockus, Stasys ^{[1
]}

Zaldarys, Gintautas ^{[1
]}

机构：

[1] Kaunas Univ Technol, Mfg Technol Dept, LT-44025 Kaunas, Lithuania

来源：

MATERIALS SCIENCE-MEDZIAGOTYRA | 2010年 / 16卷 / 04期

关键词：

ductile iron; matrix structure; section size; mechanical properties; microhardness; SPHEROIDAL GRAPHITE; MECHANICAL-PROPERTIES; NODULE COUNT; COOLING RATE; BEHAVIOR; MICROSTRUCTURE; SOLIDIFICATION; TEMPERATURE; PLATES; DAMAGE;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The relation between the kind of inoculants, the castings size and matrix structure of ductile iron was investigated. Inoculation was performed by using 4 different inoculants. Ductile iron was cast in test bars with diameters from 3 mm to 50 mm. The study of the microstructure showed that the effect of the kind of inoculant on the content of pearlite is significant only for regular specimen sizes. The hardness value was found to decrease with decreasing pearlite content in the matrix structure of ductile iron. The time between spheroidizing treatment and pouring has strong effect on the ductility of ductile iron. Ce-bearing inoculant reduced this effect. Tests were also conducted to investigate the effects of kind of inoculants and the diameter of specimens on the microhardness of pearlite. It was found that the microhardness of pearlite of small size specimens is higher than this one of large size specimens. Ce-bearing inoculant slightly equalizes pearlite contents and its microhardness in various specimens sizes.

引用

页码：307 / 310

页数：4

共 50 条

[41] EVALUATION OF PRODUCING TECHNIQUE FACTORS AFFECTING THE MATRIX MICROSTRUCTURE OF AS-CAST DUCTILE IRON CASTINGS
Bockus, S.
Zaldarys, G.
METALURGIJA, 2011, 50 (01): : 9 - 12
[42] The Effect of Ductile Cast Iron Matrix on Zinc Coating During Hot Dip Galvanising of Castings
Kopycinski, D.
Szczesny, A.
ARCHIVES OF FOUNDRY ENGINEERING, 2012, 12 (04) : 101 - 104
[43] The character of the solidification structure of massive ductile cast-iron castings and its prediction
Stransky, Karel
Dobrovska, Jana
Kavicka, Frantisek
Stetina, Josef
Sekanina, Bohumil
Franek, Zdenek
MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE V, 2008, 567-568 : 109 - +
[44] The influence of nickel content on the structure parameters and magnetic properties of austenitic ductile iron castings
Magdalena Bork
Robert Chulist
Marcin Górny
Maciej Kowalczyk
Jan Marosz
Archives of Civil and Mechanical Engineering, 25 (3)
[45] Graphite degeneration in surface layer of ductile iron castings
Ivan, N.
Chisamera, M.
Riposan, I.
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2013, 26 (03) : 138 - 142
[46] Effect of melting techniques on ductile iron castings properties
Kaunas University of Technology, Kaunas, Lithuania
不详
Metalurgija, 2006, 1 (13-16):
[47] Graphite degeneration in surface layer of ductile iron castings
POLITEHNICA University of Bucharest, 313 Spl. Independentei, RO-060042, Bucharest, Romania
Riposan, I. (riposan@foundry.pub.ro), 1600, Maney Publishing (26):
[48] Inhomogeneous Pearlite and Ferrite in Ductile Iron Sand Castings
R. N. Lumley
International Journal of Metalcasting, 2023, 17 : 1467 - 1492
[49] Effect of melting techniques on ductile iron castings properties
Bockus, S
Dobrovolskis, A
METALURGIJA, 2006, 45 (01): : 13 - 16
[50] Thin Wall Ductile Iron Castings: Technological Aspects
Fras, E.
Gorny, M.
Kapturkiewicz, W.
ARCHIVES OF FOUNDRY ENGINEERING, 2013, 13 (01) : 23 - 28

← 1 2 3 4 5 →