The B2-B19-B19′ transformation behaviour in Ti-(45-x)Ni-5Cu-xV alloys

被引：6
|
作者：
Choi, J. Y. [1 ]
Choi, E. S. [2 ]
Cho, B. S. [3 ]
Chung, Y. S. [4 ]
Nam, T. H. [1 ]
机构：
[1] Gyeongsang Natl Univ, Div Adv Mat Engn, Jinju 660701, Gyeongnam, South Korea
[2] Hongik Univ, Dept Civil Engn, Hongik, South Korea
[3] Inje Univ, Dept Civil Engn, Seoul, South Korea
[4] Chung Ang Univ, Dept Civil Engn, Seoul, South Korea
来源：
PHYSICA SCRIPTA | 2007年 / T129卷
关键词：
D O I：
10.1088/0031-8949/2007/T129/054
中图分类号：
O4 [物理学];
学科分类号：
0702 ;
摘要：
Transformation behaviour, shape memory characteristics and superelasticity of Ti-(45-x)Ni-5Cu-xV(at.%) (x = 0.5-2.0) alloys were investigated using different techniques. The B2-B19' transformation occurs when V content is less than 1.0 at.%, above which the B2-B19-B19' transformation occurs. The temperature gap between M-s' (the B2-B19 transformation start temperature) and M-s (the B19-B19' transformation start temperature) increased from 8 to 22K with increasing V content from 1.0 to 2.0 at.%. V content dependence of M-s' (the B2-B19 transformation start temperature) was 20Kat.%(-1). One-stage elongation occurred in Ti-44.5Ni-5.0Cu-0.5V and Ti-44.0Ni-5.0Cu-1.0V alloys, while two-stage elongation occurred in Ti-43.5Ni-5.0Cu-1.5V and Ti-43.0Ni-5.0Cu-2.0V alloys. Transformation hysteresis decreased from 16 to 12K with increasing V content from 0.5 to 2.0%. The superelastic recovery ratio increased from 65.0 to 86.1% with increasing V content from 0.5 to 2.0%.
引用
收藏
页码：240 / 244
页数：5
相关论文
共 50 条
  • [41] Electronic structure of B2-type Ti-(50-x)Ni-xFe and Ti-(50-x)Pd-xFe alloys exhibiting incommensurate diffuse scattering
    Yamamoto, Takuya
    Fukuda, Takashi
    Kakeshita, Tomoyuki
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 481 : 239 - 242
  • [42] Superior electrochemical performances of La-Mg-Ni alloys with A2B7/A5B19 double phase
    Fan, Yanping
    Zhang, Lu
    Xue, Chunjian
    Fan, Guangxin
    Liu, Jingjing
    Liu, Baozhong
    Han, Shumin
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2019, 44 (14) : 7402 - 7413
  • [43] Origin of the isothermal B2 B19′ transformation in NiTi-based shape memory alloys
    Belyaev, Sergey
    Resnina, Natalia
    Demidova, Elena
    Ivanov, Alexey
    Shelyakov, Alexander
    Andreev, Vladimir
    Chekanov, Valeriy
    Ubyivovk, Evgenii
    JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 902
  • [44] Influence of Ti2Cu precipitates on B19 martensite structure in a Ti-rich Ti-Ni-Cu thin film
    Meng, X. L.
    Sato, M.
    Ishida, A.
    PHILOSOPHICAL MAGAZINE LETTERS, 2008, 88 (08) : 575 - 582
  • [45] An in-situ synchrotron study of the B2→B19′ phase transformation in a Ni-Ti alloy subjected to uniaxial monotonic tension
    Bian, Xiaohui
    Saleh, Ahmed A.
    Lynch, Peter A.
    Davies, Christopher H. J.
    Pereloma, Elena V.
    Gazder, Azdiar A.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 743 : 327 - 338
  • [46] Internal friction of B2→B19′ martensitic transformation of Ti50Ni50 shape memory alloy under isothermal conditions
    Chang, S. H.
    Wu, S. K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 454 : 379 - 383
  • [47] On the lattice parameters of the B19′ martensite in binary Ti-Ni shape-memory alloys
    Prokoshkin, SD
    Brailovskii, V
    Turenne, S
    Khmelevskaya, IY
    Korotitskii, AV
    Trubitsyna, IB
    PHYSICS OF METALS AND METALLOGRAPHY, 2003, 96 (01): : 55 - 64
  • [48] Effect of thermal cycling in the range of B2-B19' phase transformation on the microstructure and mechanical properties of UFG Ti49.8Ni50.2 alloy
    Churakova, A. A.
    Gunderov, D. V.
    Lukyanov, A. V.
    Lebedev, Yu. A.
    LETTERS ON MATERIALS-PIS MA O MATERIALAKH, 2013, 3 (02): : 166 - 168
  • [49] Electropolishing conditions for trace analysis of B19′ martensite in Ti-Ni shape memory alloys
    Nishiura, T.
    Hayashi, K.
    Nishida, A.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 481 (446-451): : 446 - 451
  • [50] Precipitation of B2 and B19 phases in α2 lamella of Ti- 44.5Al-4Nb-1Mo-0.1B alloy (vol 946, 169370, 2023)
    Li, Yuqing
    Kou, Hongchao
    Wang, Yarong
    Yu, Yonghao
    Zhang, Zilong
    Li, Jinshan
    JOURNAL OF ALLOYS AND COMPOUNDS, 2023, 948
12345