Current densities of thin filament MgB2/Ti/GlidCop® wire

被引：10

作者：

Kovac, P. ^{[1
]}

Husek, I. ^{[1
]}

Melisek, T. ^{[1
]}

Kopera, L. ^{[1
]}

机构：

[1] Slovak Acad Sci, Inst Elect Engn, Bratislava 84104, Slovakia

来源：

SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 2011年 / 24卷 / 10期

关键词：

MGB2; WIRES;

D O I：

10.1088/0953-2048/24/10/105006

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Fine-filamentary MgB2/Ti/GlidCop wire has been produced by an in situ process. Hydrostatic extrusion, drawing and two-axis rolling were used for wire deformation up to the size of 0.2 x 0.2 mm(2). An averaged filament size of 7.6-14 mu m was obtained for two-axis rolled wire and tape, which are the smallest MgB2 filaments known so far. Very short annealing periods (3-7 min) were used for the thinnest filaments, resulting in a critical current density of approximate to 12 000 A cm(-2) at 8 T and 4.2 K. The results presented demonstrate the ability to prepare uniform approximate to 10 mu m size and high current density filamentary MgB2 wires in nonmagnetic sheaths, which can be applied for DC and AC coils.

引用

页数：5

共 50 条

[21] Calculated and measured normal state resistivity of 19-filament MgB2/Ti/Cu/stainless steel wire
Kopera, L.
Kovac, P.
Husek, I.
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2012, 25 (02):
[22] AC Losses of Monofilament Ti-clad MgB2 Wire
S. Safran
J. Šouc
L. Rostila
S. Brisigotti
F. Gömöry
A. Gencer
Journal of Superconductivity and Novel Magnetism, 2011, 24 : 437 - 441
[23] Crystal growth and critical current densities of polycrystalline MgB2 superconductor
Maeda, M
Mizuno, K
Takashi, A
Uchiyama, D
Kawakami, T
Kobayashi, H
Yasohama, K
Kubota, Y
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2005, 15 (02) : 3300 - 3303
[24] Critical current densities in Ag-added bulk MgB2
Muralidhar, M.
Inoue, K.
Koblischka, M. R.
Murakami, M.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2015, 518 : 36 - 39
[25] Enhanced critical current densities in Cu-sheathed MgB2
Strickland, NM
Buckley, RG
Otto, A
CURRENT APPLIED PHYSICS, 2004, 4 (06) : 688 - 692
[26] Phthalocyanine doping to improve critical current densities in MgB2 tapes
Zhang, Xianping
Ma, Yanwei
Wang, Dongliang
Gao, Zhaoshun
Wang, Lei
Qi, Yanpeng
Awaji, Satoshi
Watanabe, Kazuo
Mossang, Eric
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2009, 22 (04):
[27] Influence of the working current and temperature on quench in the superconducting wire MgB2
Surdacki, Pawel
PRZEGLAD ELEKTROTECHNICZNY, 2011, 87 (12B): : 161 - 164
[28] Influence of heat-treatment schedules on the transport current densities of long and short segments of superconducting MgB2 wire
Bhatia, M
Sumption, MD
Tomsic, M
Collings, EW
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 407 (3-4): : 153 - 159
[29] Fibrous structure and critical current density of MgB2 superconducting wire
Uchiyama, D.
Mizuno, K.
Akao, T.
Maeda, M.
Kawakami, T.
Kobayashi, H.
Kubota, Y.
Yasohama, K.
CRYOGENICS, 2007, 47 (5-6) : 282 - 286
[30] Large critical current density in MgB2 wire using MgB4 as precursor
Nardelli, D.
Matera, D.
Vignolo, M.
Bovone, G.
Palenzona, A.
Siri, A. S.
Grasso, G.
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2013, 26 (07):

← 1 2 3 4 5 →