Effect of Na2CO3 Addition on Inclusions in High-Carbon Steel for Saw Wire

被引：14

作者：

Chen, Liangjun ^{[1
]}

Chen, Weiqing ^{[1
]}

Hu, Yang ^{[1
]}

Chen, Zhaoping ^{[2
]}

Xu, Yingtie ^{[2
]}

Yan, Wei ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, State Key Lab Adv Met, Beijing 100083, Peoples R China

[2] Baoshan Iron & Steel Co Ltd, Res Inst, Shanghai 201900, Peoples R China

来源：

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2018年 / 71卷 / 02期

关键词：

Na2CO3; addition; inclusions containing Na2O; Deformability; Crystallinity; Saw wire; MN-KILLED STEEL; CORD STEEL; SLAG; DECOMPOSITION; BEHAVIOR; BILLETS;

D O I：

10.1007/s12666-017-1168-9

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Inclusions cannot be sufficiently stretched to adapt extremely strict requirement of saw wire with only conventional inclusion softening art. In order to explore a potential new method to further enhance the deformability of inclusions, Na2CO3 addition should be comprehensively investigated due to the extremely low melting temperature of inclusions containing Na2O. In the present study, an effective method of Na2CO3 addition was put forward and a presumable reaction mechanism between Na2CO3/steel/inclusion/slag was deduced by studying the effect of Fe/Na2CO3 (weight ratio), Na2CO3 addition amount and reaction time on inclusions using a graphite tube resistance furnace. The relations between Na2O content, melting temperature, deformability and crystallization of inclusions were also briefly discussed. Through these studies, the deformability of inclusions was significantly improved on the whole.

引用

页码：383 / 391

页数：9

共 50 条

[31] DENSITY VARIATION OF A HIGH-CARBON STEEL WIRE WITH WIREDRAWING STRAIN
WRIEDT, HA
HUGHES, HA
METALLURGICAL TRANSACTIONS, 1970, 1 (12): : 3457 - &
[32] DIRECTLY COOLED DRAWING OF HIGH-CARBON STEEL WIRE.
Petkovic, Dominique
Wireworld international, 1985, 27 (10): : 226 - 227
[33] High-carbon wire rod made of high-chromium steel
Sychkov, A. B.
Zhigarev, M. A.
Perchatkin, A. V.
Berkovskii, V. A.
Krulik, A. I.
METALLURGIST, 2006, 50 (3-4) : 183 - 188
[34] RAPID HEATING PATENTING OF HIGH-CARBON STEEL WIRE RODS
TAKAHASHI, E
KATO, T
ARAKAWA, J
KOUOKA, T
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1977, 17 (06) : 359 - 364
[35] Layperson's guide to drawing high-carbon steel wire
Gilliand, Roger
Springs, 37 (03):
[36] ROLLING OF HIGH-CARBON WIRE RODS IN BHILAI STEEL PLANT
BISHNOI, YPS
TUDEKAR, SG
JOURNAL OF THE IRON AND STEEL INSTITUTE, 1970, 208 (DEC): : 1083 - &
[37] High-carbon wire rod made of steel microalloyed with vanadium
Parusov, VV
Sychkov, AB
Derevyanchenko, IV
Perchatkin, AV
Parusov, ÉV
Zhigarev, MA
METALLURGIST, 2004, 48 (11-12) : 618 - 625
[38] High-carbon wire rod made of steel microalloyed with vanadium
V. V. Parusov
A. B. Sychkov
I. V. Derevyanchenko
A. V. Perchatkin
É. V. Parusov
M. A. Zhigarev
Metallurgist, 2004, 48 : 618 - 625
[39] THE EFFECT OF CENTER LINE SEGREGATION ON THE MICROMARTENSITE APPEARANCE IN HIGH-CARBON STEEL WIRE ROD
TAKAHASHI, T
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (13): : 1310 - 1310
[40] EFFECT OF ALLOYING ELEMENTS ON MECHANICAL-PROPERTIES OF HIGH-CARBON STEEL WIRE ROD
TAMAI, Y
EGUCHI, T
TEZUKA, K
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 24 (08) : B280 - B280

← 1 2 3 4 5 →