Effect of Na2CO3 Addition on Inclusions in High-Carbon Steel for Saw Wire

被引：14

作者：

Chen, Liangjun ^{[1
]}

Chen, Weiqing ^{[1
]}

Hu, Yang ^{[1
]}

Chen, Zhaoping ^{[2
]}

Xu, Yingtie ^{[2
]}

Yan, Wei ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, State Key Lab Adv Met, Beijing 100083, Peoples R China

[2] Baoshan Iron & Steel Co Ltd, Res Inst, Shanghai 201900, Peoples R China

来源：

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2018年 / 71卷 / 02期

关键词：

Na2CO3; addition; inclusions containing Na2O; Deformability; Crystallinity; Saw wire; MN-KILLED STEEL; CORD STEEL; SLAG; DECOMPOSITION; BEHAVIOR; BILLETS;

D O I：

10.1007/s12666-017-1168-9

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Inclusions cannot be sufficiently stretched to adapt extremely strict requirement of saw wire with only conventional inclusion softening art. In order to explore a potential new method to further enhance the deformability of inclusions, Na2CO3 addition should be comprehensively investigated due to the extremely low melting temperature of inclusions containing Na2O. In the present study, an effective method of Na2CO3 addition was put forward and a presumable reaction mechanism between Na2CO3/steel/inclusion/slag was deduced by studying the effect of Fe/Na2CO3 (weight ratio), Na2CO3 addition amount and reaction time on inclusions using a graphite tube resistance furnace. The relations between Na2O content, melting temperature, deformability and crystallization of inclusions were also briefly discussed. Through these studies, the deformability of inclusions was significantly improved on the whole.

引用

页码：383 / 391

页数：9

共 50 条

[1] Effect of Na2CO3 Addition on Inclusions in High-Carbon Steel for Saw Wire
Liangjun Chen
Weiqing Chen
Yang Hu
Zhaoping Chen
Yingtie Xu
Wei Yan
Transactions of the Indian Institute of Metals, 2018, 71 : 383 - 391
[2] Effects of K2CO3 Addition on Inclusions in High-Carbon Steel for Saw Wire
Chen, Liangjun
Chen, Weiqing
Hu, Yang
Chen, Zhaoping
Xu, Yingtie
Yan, Wei
HIGH TEMPERATURE MATERIALS AND PROCESSES, 2018, 37 (08) : 701 - 709
[3] EFFECT OF VANADIUM ADDITION ON STRENGTH AND DUCTILITY OF HIGH-CARBON STEEL WIRE ROD
MAJIMA, H
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1396 - 1396
[4] Effect of cerium addition on non-metallic inclusions in a high-carbon chromium bearing steel
Li, Hao
Ren, Qiang
Zhang, Li-feng
JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2023, 30 (11) : 2254 - 2266
[5] Effect of cerium addition on non-metallic inclusions in a high-carbon chromium bearing steel
Hao Li
Qiang Ren
Li-feng Zhang
Journal of Iron and Steel Research International, 2023, 30 : 2254 - 2266
[6] Effect of Al antioxidant in MgO-C refractory on the formation of Al2O3-rich inclusions in high-carbon steel for saw wire under vacuum conditions
Chen, L.
Chen, W.
Hu, Y.
Chen, Z.
Xu, Y.
Yan, W.
IRONMAKING & STEELMAKING, 2018, 45 (03) : 272 - 279
[7] THE EFFECT OF DRAWING SPEED ON THE AGEING OF HIGH-CARBON STEEL WIRE
Suliga, M.
ARCHIVES OF METALLURGY AND MATERIALS, 2018, 63 (04) : 1931 - 1935
[8] Modification of Alumina Inclusions in High-Carbon Hard Wire Steel by Rare Earth Yttrium
Xiong X.
Li C.
Chen L.
Chen L.
Ning Z.
Xiyou Jinshu/Chinese Journal of Rare Metals, 2024, 48 (04): : 508 - 516
[9] TORSIONAL DUCTILITY OF HIGH-CARBON STEEL WIRE
HALLGARTH, JK
IRONMAKING & STEELMAKING, 1995, 22 (03) : 211 - 222
[10] Hydration of the cement paste with Na2CO3 addition
Janotka, I
CERAMICS-SILIKATY, 2001, 45 (01) : 16 - 23

← 1 2 3 4 5 →