Corrosion-fatigue crack propagation of aluminum alloys for high-speed trains

被引：9
|
作者：
Shen, Lin [1 ]
Chen, Hui [1 ]
Che, Xiaoli [1 ]
Xu, Lidong [1 ]
机构：
[1] Southwest Jiaotong Univ, Sch Mat Sci & Engn, Chengdu 610031, Sichuan, Peoples R China
来源：
INTERNATIONAL JOURNAL OF MODERN PHYSICS B | 2017年 / 31卷 / 16-19期
关键词：
Aluminum alloy; corrosion fatigue; crack propagation; high-speed train; ENVIRONMENT; STRENGTH;
D O I：
10.1142/S021797921744009X
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
A modified single-edge notch tension (SENT) specimen exposed to saline environment was utilized to investigate the corrosion fatigue crack growth behaviors of 5083, 6005 and 7N01 aluminum alloys. The fatigue crack propagation life, corrosion fatigue crack rate (da/dN) were tested. The microstructures and fracture surfaces of specimens were examined by optical microscopy and scanning electron microscopy (SEM). The results showed that fatigue crack propagation rate of 7N01 in 3.5% NaCl was significantly higher than 6005 and 5083 alloys. The mechanisms of anodic dissolution and hydrogen embrittlement are used to explain the results.
引用
收藏
页数：7
相关论文
共 50 条
  • [21] CORROSION-FATIGUE CRACK PROPAGATION STUDIES OF SOME NEW HIGH-STRENGTH STRUCTURAL STEELS
    CROOKER, TW
    LANGE, EA
    [J]. MECHANICAL ENGINEERING, 1969, 91 (08): : 70 - &
  • [22] Corrosion-fatigue interactions for high strength aluminium alloys
    Dif, R
    Ehrström, JC
    [J]. ALUMINUM ALLOYS 2002: THEIR PHYSICAL AND MECHANICAL PROPERTIES PTS 1-3, 2002, 396-4 : 1285 - 1290
  • [23] Propagation of corrosion induced fatigue crack in aluminum alloy
    Kumar, Pawan
    Verma, B. B.
    [J]. AIMS MATERIALS SCIENCE, 2022, 9 (03) : 512 - 521
  • [24] THE INFLUENCE OF LOADING WAVE-FORM ON CORROSION-FATIGUE CRACK-PROPAGATION
    WANG, ZF
    LI, J
    WANG, JQ
    KE, W
    [J]. CORROSION SCIENCE, 1995, 37 (10) : 1551 - 1565
  • [25] STRUCTURAL INTERPRETATION OF FATIGUE CRACK PROPAGATION IN ALUMINUM ALLOYS
    CROOKER, TW
    [J]. REPORT OF NRL PROGRESS, 1971, (MAR): : 27 - &
  • [26] SECONDARY DAMAGE IN CORROSION-FATIGUE OF ALUMINUM
    DANIELS, RD
    LORKOVIC, WM
    [J]. METALLURGICAL TRANSACTIONS, 1971, 2 (07): : 1990 - &
  • [27] On the Micromechanisms of Fatigue Crack Propagation in Aluminum Cast Alloys
    Krupp, U.
    Giertler, A.
    Siegfanz, S.
    Michels, W.
    [J]. MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE VII, 2014, 592-593 : 393 - 396
  • [28] FATIGUE FRACTURE AND CRACK PROPAGATION IN ALUMINUM ALLOYS.
    Kohara, Shiro
    Muto, Norio
    [J]. 1600, (08):
  • [29] ENVIRONMENTAL-EFFECTS ON CRACK CLOSURE IN THE CORROSION-FATIGUE OF AN ALUMINUM - LITHIUM ALLOY
    PYUN, SI
    CHUN, YG
    [J]. CORROSION SCIENCE, 1993, 35 (1-4) : 611 - 619
  • [30] Rail fatigue crack propagation in high-speed wheel/rail rolling contact
    Jiang X.
    Li X.
    Li X.
    Cao S.
    [J]. Journal of Modern Transportation, 2017, 25 (3): : 178 - 184
12345