The effect of single overloads in tension and compression on the fatigue crack propagation behaviour of short cracks

被引：17
|
作者：
Zhou, Xiang [1 ,2 ]
Gaenser, Hans-Peter [1 ]
Pippan, Reinhard [2 ,3 ]
机构：
[1] Mat Ctr Leoben Forsch GmbH, Roseggerstr 12, A-8700 Leoben, Austria
[2] Austrian Acad Sci, Erich Schmid Inst Mat Sci, Jahnstr 12, A-8700 Leoben, Austria
[3] Univ Leoben, Dept Mat Phys, Jahnstr 12, A-8700 Leoben, Austria
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2016年 / 89卷
关键词：
Overload; Crack closure; Residual stress; Threshold of stress intensity; Effective threshold; FINITE-ELEMENT ANALYSIS; GROWTH; CLOSURE; THRESHOLD; METALS; STEEL;
D O I：
10.1016/j.ijfatigue.2016.02.001
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The crack propagation behaviour in cast quenched and tempered steel after one overload cycle in tension as well as in compression on short cracks is investigated in deep notched specimens. The overload cycle exhibits a significant influence on the fatigue life endurance, due to the formation of an overload plastic zones in front of the crack tip. The crack propagation after overload cycles is investigated by inspection of the fatigue threshold R-curve and fatigue crack propagation rate. Tension overload increased the long crack threshold and reduced the R-curve effect, whereas overloads in compression reduced the crack growth resistance and shifted the threshold value to larger crack extension. A simple FE simulation was also performed to investigate the variation in the contribution of plasticity induced crack closure during crack propagation after the overload. Macroscopic mechanistic and dislocation models are introduced to explain the results obtained. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：77 / 86
页数：10
相关论文
共 50 条
  • [41] Dislocation model for fatigue crack propagation of long cracks
    Pippan, R
    Riemelmoser, FO
    KOVOVE MATERIALY-METALLIC MATERIALS, 1998, 36 (03): : 183 - 192
  • [42] Crack retardation equations for the propagation of branched fatigue cracks
    Meggiolaro, MA
    Miranda, ACO
    Castro, JTP
    Martha, LF
    INTERNATIONAL JOURNAL OF FATIGUE, 2005, 27 (10-12) : 1398 - 1407
  • [43] FATIGUE CRACK CLOSURE IN KINKED CRACKS AND PATH OF CRACK-PROPAGATION
    MAGEED, AMA
    PANDEY, RK
    INTERNATIONAL JOURNAL OF FRACTURE, 1990, 44 (03) : R39 - R42
  • [44] Crack growth rate of concrete with pre-cracks in tension-compression cyclic fatigue load
    Shen, J. (shen03liu01@163.com), 1600, Tongji University (17):
  • [45] On propagation of short rolling contact fatigue cracks
    Ringsberg, JW
    Bergkvist, A
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2003, 26 (10) : 969 - 983
  • [46] The effect of compression loading on fatigue crack propagation after a single tensile overload at negative stress ratios
    Bai, Shigang
    Sha, Yu
    Zhang, Jiazhen
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 110 : 162 - 171
  • [47] An experimental study on fatigue crack propagation under cyclic loading with multiple overloads
    Kim, KS
    Cho, DI
    Ahn, JW
    Choi, SB
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 2495 - 2500
  • [48] CRACK INITIATION UNDER FAR-FIELD CYCLIC COMPRESSION AND THE STUDY OF SHORT FATIGUE CRACKS
    CHRISTMAN, T
    SURESH, S
    ENGINEERING FRACTURE MECHANICS, 1986, 23 (06) : 953 - 964
  • [49] Fatigue crack growth behaviour of surface cracks in Glare
    Alderliesten, RC
    Homan, JJ
    FATIGUE DAMAGE OF MATERIALS: EXPERIMENT AND ANALYSIS, 2003, 5 : 213 - 222
  • [50] Analytical Prediction Model for Fatigue Crack Propagation Rate under Tension-Compression Loading
    Sha Yu
    Bai Shigang
    Wang Yahui
    MATERIALS, MECHANICAL AND MANUFACTURING ENGINEERING, 2014, 842 : 455 - +
12345