Physical and magnetic properties, microstructure of bonded magnet NdFeB prepared by using synthesis rubber

The magnet permanent has been made by using NdFeB (NQP-B) powder with purity 99.90 % and polymer rubber with purity 90%. This research was done to determine the effect of the polymer (rubber) composition as binder in the manufacture of bonded magnet NdFeB on physical properties, microstructure and magnetic properties. Bonded magnets are magnet material made from a mixture of magnetic powder as a filler and the polymer as a matrix material or as binder to bind the magnetic particles. The NdFeB (NQP-B) powder fractions of bonded magnets NdFeB investigated were as follows: a) 97 wt.% of NdFeB (NQP-B) and 3 wt.% of rubber, b) 95wt.% of NdFeB (NQP-B) and 5 wt.% of rubber, c) 93 wt.% of NdFeB (NQP-B) and 7 wt.% of rubber, d) 91 wt.% of NdFeB (NQP-B) and 9 wt.% of rubber. Both raw materials were mixed by using mixer until homogen with total weight about 16 g for each sample, then added 0.3 ml of catalyst and mixed again and put in dies mould and compacted at pressure 30 MPa, then dried for 2 hours at room temperature. The dried samples was characterized such as : bulk density measurement and magnetic properties by using BH-curve permeagraph. The bulk density values of the sample bonded NdFeB magnets using the binder 3% wt. and 5% wt. rubber are respectively 4,70 g/cm(3) and 4.88 g/cm(3). The result from BH-curve shows that the highest value of remanence (Br = 5.12 kGauss) is at sample with 3 % wt. of rubber, but sample with 5 % wt. of rubber has lowest value of remanance (Br = 4.40 kGauss). Based on the observation of the SEM photograph shown that the rubber material has been successfully covered the whole surface of the grain and fill some of the voids that are in the grain boundary.