Mechanical properties of porous Ti-15Mo-5Zr-3Al compacts prepared by powder sintering

被引：50

作者：

Nomura, N ^{[1
]}

Kohama, T

Oh, IH

Hanada, S

Chiba, A

Kanehira, M

Sasaki, K

机构：

[1] Iwate Univ, Dept Welfare Engn, Morioka, Iwate 0208551, Japan

[2] Tohoku Univ, Grad Sch Mat Sci, Sendai, Miyagi 9808579, Japan

[3] Korea Inst Ind Technol, Mat & Parts Team, Kwangju 506824, South Korea

[4] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan

[5] Tohoku Univ, Grad Sch Dent, Sendai, Miyagi 9808575, Japan

来源：

MATERIALS SCIENCE & ENGINEERING C-BIOMIMETIC AND SUPRAMOLECULAR SYSTEMS | 2005年 / 25卷 / 03期

关键词：

porous titanium alloy; PREP; hot-pressing; Young's modulus; yield strength;

D O I：

10.1016/j.msec.2005.04.001

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Porous Ti alloy compacts were fabricated and their microstructure and mechanical properties were investigated in this study. Ti alloy powders were atomized from Ti-15Mo-5Zr-3Al (wt.%) bar using the plasma rotating electrode process (PREP) in an Ar atmosphere. These alloy powders were sintered under 1-30 MPa at 1223 K for 7.2 ks by hot-pressing (HP). These compacts were solution treated at 1223 K for 1.2 ks, and then quenched into iced water (STQ). X-ray diffraction analysis revealed that a small amount of alpha phase appeared in the beta phase of the HP compacts, while not in the STQ compacts. Young's modulus of STQ compacts is lower than that of HP compacts. It was found that the strength of porous Ti-15Mo-5Zr-3Al is higher than those of porous pure Ti and human cortical bone, as compared in the range from 10 to 30 GPa of Young's modulus for human bone. (c) 2005 Elsevier B.V All rights reserved.

引用

页码：330 / 335

页数：6

共 50 条

[21] Stability of vacancies in 6-type Ti-15Mo-5Zr-3Al alloy fabricated via laser powder bed fusion
Mizuno, Masataka
Sugita, Kazuki
Do, Kousuke
Ishimoto, Takuya
Nakano, Takayoshi
Araki, Hideki
ADDITIVE MANUFACTURING LETTERS, 2023, 7
[22] THE EFFECT OF COLD DRAWING AND AGING ON THE STRENGTH OF TI-15MO-5ZR-3AL AND TI-13V-11CR-3AL
MATSUMOTO, T
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 73 (05): : S699 - S699
[23] Phase Transformation of a Ti-15Mo-5Zr-3Al Brazed Joint Using Clad Ti-15Cu-15Ni Filler
Yue, Gui-Lin
Chen, Tai-Cheng
Shiue, Ren-Kae
Tsay, Leu-Wen
METALS, 2020, 10 (01)
[24] High strain rate deformation of Ti-15Mo-5Zr-3Al alloy over wide temperature range
Lee, W. -S.
Lin, C. -F.
Chen, T. -H.
Hwang, H. -H.
MATERIALS SCIENCE AND TECHNOLOGY, 2008, 24 (01) : 15 - 25
[25] Bone integration capability of alkali- and heat-treated nanobimorphic Ti-15Mo-5Zr-3Al
Tsukimura, Naoki
Ueno, Takeshi
Iwasa, Fuminori
Minamikawa, Hajime
Sugita, Yoshihiko
Ishizaki, Ken
Ikeda, Takayuki
Nakagawa, Kaori
Yamada, Masahiro
Ogawa, Takahiro
ACTA BIOMATERIALIA, 2011, 7 (12) : 4267 - 4277
[26] Mean stress dependence of fatigue strength and subsurface crack initiation in Ti-15Mo-5Zr-3Al alloy
Tokaji, K
Kariya, H
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 281 (1-2): : 268 - 274
[27] Dissimilar Brazing of Ti-15Mo-5Zr-3Al and Commercially Pure Titanium Using Ti-Cu-Ni Foil
Yue, Gui-Lin
Chen, Tai-Cheng
Shiue, Ren-Kae
Tsay, Leu-Wen
MATERIALS, 2021, 14 (20)
[28] Microstructural and Orientation Dependence of the Plastic Deformation Behavior in β-type Ti-15Mo-5Zr-3Al Alloy Single Crystals
Sang-Hoon Lee
Koji Hagihara
Takayoshi Nakano
Metallurgical and Materials Transactions A, 2012, 43 : 1588 - 1597
[29] KINETICS OF THE PHASE-TRANSFORMATION IN A TI-15MO-5ZR-3AL ALLOY AS STUDIED BY X-RAY-DIFFRACTION
RAO, VB
HOUSKA, CR
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (03): : 355 - 358
[30] Microstructural and Orientation Dependence of the Plastic Deformation Behavior in β-type Ti-15Mo-5Zr-3Al Alloy Single Crystals
Lee, Sang-Hoon
Hagihara, Koji
Nakano, Takayoshi
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (05): : 1588 - 1597

← 1 2 3 4 5 →