Effect of Adipic Acid on DEIS Characteristics during the Aluminium Anodizing Process in Sulfuric Acid Bath

被引：0
|
作者：
Hua, Lei [1 ]
Liu, Jianhua [1 ]
Li, Songmei [1 ]
Yu, Mei [1 ]
机构：
[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100191, Peoples R China
来源：
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2015年 / 10卷 / 03期
关键词：
Aluminum; Adipic-sulfuric acid anodizing; DEIS; Interface reaction; ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY; POINT-DEFECT MODEL; OXIDE-FILMS; CORROSION-RESISTANCE; PURE ALUMINUM; ALLOY; BEHAVIOR; SPECTRA; MEDIA;
D O I：
暂无
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
The formation process of anodic film on aluminium was investigated in the bath containing adipic acid and sulfuric acid (ASA bath) by using dynamic electrochemical impedance spectroscopy (DEIS). An interface reaction and ionic migration mechanism of anodic oxidation process in the ASA bath was established to interpreting the DEIS data. The impedance was decrease with the addition of adipic acid added in the anodizing bath, because of the adsorption of adipic anions on the surface of oxide film. An electrical equivalent circuit (EEC) model was established to analyse the relationship of the EEC model elements with the applied potential. The results indicated that the addition of adipic acid into the anodizing bath was beneficial to the grown of oxide film on aluminium, like faster in grown rate and thicker in thickness.
引用
收藏
页码：2194 / 2205
页数：12
相关论文
共 50 条
  • [31] On a combination of aluminium sulphate and sulfuric acid
    Baud, E
    COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES, 1903, 137 : 492 - 494
  • [32] Evolution of insoluble eutectic Si particles in anodic oxidation films during adipic-sulfuric acid anodizing processes of ZL114A aluminum alloys
    Lei Hua
    Jian-hua Liu
    Song-mei Li
    Mei Yu
    Lei Wang
    Yong-xin Cui
    International Journal of Minerals, Metallurgy, and Materials, 2015, 22 : 302 - 308
  • [33] Evolution of insoluble eutectic Si particles in anodic oxidation films during adipic-sulfuric acid anodizing processes of ZL114A aluminum alloys
    Hua, Lei
    Liu, Jian-hua
    Li, Song-mei
    Yu, Mei
    Wang, Lei
    Cui, Yong-xin
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2015, 22 (03) : 302 - 308
  • [34] A SULFURIC-ACID BATH FOR ELECTROPLATING PALLADIUM
    SIMON, F
    ZILSKE, W
    PLATING AND SURFACE FINISHING, 1982, 69 (06): : 86 - 89
  • [35] Evaluation of Durability Depending on Two Step Anodizing Process Time Using Sulfuric Acid Electrolyte
    Lee, Seung-Jun
    Kim, Seong-Jong
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2019, 19 (04) : 2291 - 2294
  • [36] Complex influence of temperature on oxalic acid anodizing of aluminium
    Leontiev, A. P.
    Roslyakov, I., V
    Napolskii, K. S.
    ELECTROCHIMICA ACTA, 2019, 319 : 88 - 94
  • [37] The influence of "Light green" additive on the anodizing of aluminum in sulfuric acid
    Dimogerontakis, T
    Tsangaraki-Kaplanoglou, I
    PLATING AND SURFACE FINISHING, 2003, 90 (05): : 80 - 82
  • [38] Citric Acid as an Alternative to Sulfuric Acid for the Hard-Anodizing of AA6061
    Cabral-Miramontes, Jose
    Almeraya-Calderon, Facundo
    Lopez, Francisco Estupinan
    Lara Banda, Maria
    Olguin-Coca, Javier
    Lopez-Leon, Luis Daimir
    Castaneda-Robles, Ivan
    Esneider Alcala, Miguel Angel
    Zambrano-Robledo, Patricia
    Gaona-Tiburcio, Citlalli
    METALS, 2021, 11 (11)
  • [39] Practical effects of unclogging pores with AC power during aluminum anodizing in sulfuric acid electrolytes
    Lerner, M
    PLATING AND SURFACE FINISHING, 2002, 89 (02): : 38 - 41
  • [40] ELECTROCATALYTIC ANODES FOR ZINC ELECTROWINNING BY METHANOL DEPOLARIZATION PROCESS IN SULFURIC ACID BATH.
    Mushiake, Katsuhiko
    Masuko, Noboru
    Takahashi, Masao
    Nihon Kogyokaishi, 1985, 101 (1174): : 787 - 793
12345