Preparation, and magnetic and electromagnetic properties of La-doped strontium ferrite films

SrLaxFe12-xO19 films (x=0-1.0) with large magneto-crystalline anisotropy were synthesized on SiO2 substrate by sol-gel and self-propagating high-temperature synthesis technique. The films were characterized by various experimental techniques including X-ray diffraction analysis, Field Emission Scanning Electron Microscope, Atomic Force Microscopy, Vibrating Sample Magnetometry and vector network analyzer. The results show that La ions completely enter into strontium ferrite lattice without changing the ferrite appearance; its grain size is approximately 40-80 nm, its length is 100 nm; the magnetoplumbite structure is proved through testing a concertina form of the crystal grain; the maximum coercivity is 5986 Oe at x=0.2; La-doped films possess a wider microwave absorption frequency range with better gross loss angle tangent (tan delta > 0.1), from 9 to 10.5 GHz at x=0.2, where the maximum value of tan delta reaches 0.2709. The La-doped films reach smaller nanometer size, better magnetic properties and microwave absorption properties with the doping of lanthanum. Crown Copyright (C) 2011 Published by Elsevier B.V. All rights reserved.