Post Mechanical Shock Test Failure Analysis on Mixed SnAgCu-BiSn BGA Solder Joints

被引：0
|
作者：
Aspandiar, R. [1 ]
Murayama, K. [2 ]
Goonetilleke, P. [1 ]
Radhakrishnan, J. [3 ]
Fu, H. [4 ]
机构：
[1] Intel Corp, Hillsboro, OR 97229 USA
[2] Shinko Elect Ind Co LTD, Nagano 3810014, Japan
[3] Intel Corp, Folsom, CA 95630 USA
[4] iNEMI, Shanghai 200031, Peoples R China
来源：
2021 INTERNATIONAL CONFERENCE ON ELECTRONICS PACKAGING (ICEP 2021) | 2021年
关键词：
Low Temperature Solder; BGA solder joints; Bi-Sn metallurgy; Mechanical Drop Shock Reliability;
D O I：
暂无
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Drop Shock Reliability of mixed alloy SnAgCu-BiSn Flip Chip BGA solder joints assembled on a Shock Test Board with two different surface finishes (Cu Organic Solderability Protectant and Electroless Nickel Immersion Gold) using three different categories of BiSn solder pastes was investigated. A metallographic analysis of the failed solder joints was undertaken to ascertain location of the cracks, their propagation paths, and to characterize microstructural features close to the cracks. Results indicated all failures occurred close to the solder-to-board land interface. The diminished reliability of solder joints on the nickel-gold based surface finish was determined to be due to the crack propagation pathway being between the intermetallic compounds and the Ni(P) layer. For the copper surface finish, the crack pathway was within the solder just above the intermetallic compound layer, and this resulted in a higher shock resistant solder joint. Bi wt% analysis in the crack region revealed that the enhancement of the solder ductility by minor quantities of elemental additions more than compensated for the higher localized Bi wt% concentration near the board lands, improving the solder joint shock reliability.
引用
收藏
页码：137 / 138
页数：2
相关论文
共 38 条
  • [11] Failure Analysis and Modeling of Solder Joints in BGA Packaged Electronic Chips
    Chen, Yaojun
    Jing, Bo
    Li, Jianfeng
    Jiao, Xiaoxuan
    Hu, Jiaxing
    Wang, Yun
    IEEE TRANSACTIONS ON COMPONENTS PACKAGING AND MANUFACTURING TECHNOLOGY, 2021, 11 (01): : 43 - 50
  • [12] Shock fatigue damage failure boundary study of BGA solder joints based on shock response spectrum
    Dang, Yongbin
    Sun, Yi
    Hao, Zhiwei
    Zhang, Qiuhua
    Liu, Wei
    Yang, Chaozhi
    INTERNATIONAL JOURNAL OF FATIGUE, 2024, 182
  • [13] Finite element analysis and fatigue life prediction of BGA mixed solder joints
    Ting-biao, Jiang
    Chao, Du
    Long-hui, Xu
    HDP'07: PROCEEDINGS OF THE 2007 INTERNATIONAL SYMPOSIUM ON HIGH DENSITY PACKAGING AND MICROSYSTEM INTEGRATION, 2007, : 281 - +
  • [14] A coupled numerical and experimental study on thermo-mechanical fatigue failure in SnAgCu solder joints
    Erinc, M.
    Schreurs, P. J. G.
    Geers, M. G. D.
    EUROSIME 2007: THERMAL, MECHANICAL AND MULTI-PHYSICS SIMULATION AND EXPERIMENTS IN MICRO-ELECTRONICS AND MICRO-SYSTEMS, PROCEEDINGS, 2007, : 707 - +
  • [15] The Simulation Analysis for the Correlation between Failure of BGA Solder Joints and the Loading Modes
    Wang Lifeng
    He Bing
    Yu Yangyang
    2014 15TH INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY (ICEPT), 2014, : 933 - 936
  • [16] Failure Analysis Technology of Lead-free BGA Solder Joints and Relevant Cases
    Tian Wanchun
    Wu Qin
    Zhou Liang
    2018 19TH INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY (ICEPT), 2018, : 284 - 287
  • [17] Vibration analysis of low temperature BGA and LGA solder joints at elevated test temperatures
    Anselm, Martin K.
    Lakshminarayan, Nithin
    Meilunas, Michael
    MICROELECTRONICS RELIABILITY, 2025, 165
  • [18] SnAgCu micro-ball grid array (BGA) solder joint evaluation using a torsion mechanical fatigue test method
    Ryan, Claire
    Rodgers, Bryan A.
    Punch, Jeff M.
    ADVANCES IN ELECTRONIC PACKAGING 2005, PTS A-C, 2005, : 1223 - 1228
  • [19] iNEMI Project on Process Development of BiSn-Based Low Temperature Solder Pastes Part III: Mechanical Shock Tests on POP BGA Assemblies
    Fu, Haley
    Radhakrishnan, Jagadeesh
    Ribas, Morgana
    Aspandiar, Raiyo
    Byrd, Kevin
    Chen, Jimmy
    Cheng, Shunfeng
    Chen, Qin
    Coyle, Richard
    Feng, Sophia
    Krmpotich, Mark
    Mokler, Scott
    Sandy-Smith, Brook
    Tang, Kok Kwan
    Wu, Greg
    Zhang, Anny
    Zhen, Wilson
    2018 INTERNATIONAL CONFERENCE ON ELECTRONICS PACKAGING AND IMAPS ALL ASIA CONFERENCE (ICEP-IAAC), 2018, : 13 - 18
  • [20] Drop Test Failure Analysis of SAC BGA solder joints using Ni/Au and Cu-OSP pad finish
    Xie Xiaoqiang
    Wang Lei
    Lee, Taekoo
    ICEPT: 2006 7TH INTERNATIONAL CONFERENCE ON ELECTRONICS PACKAGING TECHNOLOGY, PROCEEDINGS, 2006, : 842 - +
1234