Electrical and optical characterization of CdTe solar cells with CdS and CdSe butters-A comparative study

A study is reported comparing the electrical and optical properties of CdTe solar cells, prepared using CdS and CdSe buffer layers, to investigate defects in the bulk and interface, carrier transport, and recombination. Temperature dependent capacitance-voltage measurement and admittance spectroscopy were used to extract carrier concentration, resistivity, charge carrier mobility, and their temperature dependence. The authors identify the presence of two defect signatures corresponding to carrier freeze-out and the formation of a Schottky back-contact barrier. The back-contact barrier height (approximate to 300 meV) extracted from the temperature dependent current density-voltage (JVT) experiment was confirmed by conventional admittance spectroscopy. The activation energies of mobility (resistivity) are 101.2 +/- 2.5 meV (92.6 +/- 2.3 meV) and 84.7 +/- 2.7 meV (77.6 +/- 4.5 meV) for CdS and CdSe buffer layers, respectively. Intensity dependent photoluminescence analysis demonstrates that the CdSe/CdTe device exhibits lower radiative efficiency than the CdS/CdTe device. This confirms the presence of higher defects in the CdSe/CdTe device corroborated by temperature dependent V-OC analysis. The comparative electrical and optical analysis provides insight into improving the performance of CdTe solar cell device by selenization. Published by the AVS.