Research on the road performance of resin bio-oil mixtures

被引：4
|
作者：
Zhu, Yiming [1 ,2 ]
Pei, Zhongshi [1 ]
Yi, Junyan [1 ]
Zhou, Wenyi [1 ]
Ai, Xinman [1 ]
Feng, Decheng [1 ]
机构：
[1] Harbin Inst Technol, Sch Transportat Sci & Engn, 73 Huanghe Rd, Harbin 150090, Peoples R China
[2] Zhejiang Inst Commun Co LTD, 928 Yuhangtang Rd, Hangzhou 310000, Peoples R China
来源：
CONSTRUCTION AND BUILDING MATERIALS | 2021年 / 302卷
关键词：
Resin bio-oil mixture; Dynamic modulus; Flow test; Semicircular bend test; Performance investigation; BITUMINOUS BINDERS; ASPHALT BINDERS;
D O I：
10.1016/j.conbuildmat.2021.124162
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
In recent years, resin asphalt and bio-oil have been widely used to improve various properties of asphalt concrete. The road performance of homemade resin bio-oil able to completely replace petroleum asphalt was explored in this study. The homemade resin bio-oil, 90# neat asphalt, and SBS-modified asphalt were used to perform the Marshall test to determine the mix ratio and optimal binder content. Then, the three kinds of mixtures were tested for dynamic modulus, flow test, and semicircular bend tests to explore their road performance. The experimental results show that the homemade resin bio-oil mixture has better resistance to deformation at high temperature and incomparable crack resistance under extremely low temperature conditions compared with the other two kinds of petroleum asphalt mixtures.
引用
收藏
页数：14
相关论文
共 50 条
  • [31] The effect of support on the catalytic performance for bio-oil upgrading
    Ma, Zhongyi
    Wei, Lin
    Qu, Wangda
    Juson, James
    Zhu, Qingwei
    Wang, Xunzhang
    PROGRESS IN RENEWABLE AND SUSTAINABLE ENERGY, PTS 1 AND 2, 2013, 608-609 : 350 - +
  • [32] Effect of bio-oil on the tribological performance of engine cylinder
    Xu, Yu-Fu
    Hu, Xian-Guo
    Yu, Hui-Qiang
    Zhang, Dan-Yang
    Xue, Teng
    Wei, Xiao-Yang
    Mocaxue Xuebao/Tribology, 2013, 33 (05): : 514 - 521
  • [33] Multicomponent vaporization modeling of bio-oil and its mixtures with other fuels
    Zhang, Lei
    Kong, Song-Charng
    FUEL, 2012, 95 (01) : 471 - 480
  • [34] Performance evaluation of asphalt mixtures containing high-RAP binder content and bio-oil rejuvenator
    Mirhosseini, Ali Foroutan
    Tahami, Seyed Amid
    Hoff, Inge
    Dessouky, Samer
    Ho, Chun-Hsing
    CONSTRUCTION AND BUILDING MATERIALS, 2019, 227
  • [35] Investigating the Field Performance of High- Recycled Asphalt Pavement Mixtures with Bio-oil Recycling Agent
    Bastola, Nitish R.
    Khedmati, Mahdieh
    Yazdipanah, Farzad
    Haghshenas, Hamzeh F.
    TRANSPORTATION RESEARCH RECORD, 2024, : 1004 - 1014
  • [36] Importance of hydrogen and bio-oil inlet temperature during the hydrotreatment of bio-oil
    Gholizadeh, Mortaza
    Gunawan, Richard
    Hu, Xun
    Kadarwati, Sri
    Westerhof, Roel
    Chaiwat, Weerawut
    Hasan, Md Mahmudul
    Li, Chun-Zhu
    FUEL PROCESSING TECHNOLOGY, 2016, 150 : 132 - 140
  • [37] Toward Understanding of Bio-Oil Aging: Accelerated Aging of Bio-Oil Fractions
    Meng, Jiajia
    Moore, Andrew
    Tilotta, David
    Kelley, Stephen
    Park, Sunkyu
    ACS SUSTAINABLE CHEMISTRY & ENGINEERING, 2014, 2 (08): : 2011 - 2018
  • [38] Investigation of aging performance of bio-oil phenol-formaldehyde resin with the treatment of artificial accelerated aging method
    Yu, Yuxiang
    Xu, Pingping
    Xing, Jingchen
    Li, Lufei
    Chang, Jianming
    POLYMER ENGINEERING AND SCIENCE, 2018, 58 (10): : 1810 - 1816
  • [39] Catalytic upgrading of bio-oil by ZnCl2 exchanged resin with microwave
    Zhang, Feng
    Jiang, Xiao-Yuan
    Lou, Hui
    Zheng, Xiao-Ming
    Ranliao Huaxue Xuebao/Journal of Fuel Chemistry and Technology, 2011, 39 (12): : 901 - 906
  • [40] The Use of Environmentally Friendly Bio-Oil in the Production of Phenol Formaldehyde (PF) Resin
    Omar, Naja Nadiera
    Mustafa, Iskandar Shahrim
    Abdullah, Nurhayati
    Hashim, Rokiah
    PERTANIKA JOURNAL OF SCIENCE AND TECHNOLOGY, 2018, 26 (01): : 177 - 191
12345