Hydrogen embrittlement on fracture resistance of low-alloy reactor pressure vessel steel with high dynamic strain aging at 288 °C

被引：3
|
作者：
Que, Z. [1 ,2 ]
Seifert, H. P. [1 ]
Mazanova, V [1 ,3 ,4 ]
Spatig, P. [1 ]
机构：
[1] Paul Scherrer Inst, Lab Nucl Mat, CH-5232 Villigen, Switzerland
[2] VTT Tech Res Ctr Finland, Espoo 02044, Finland
[3] Czech Acad Sci, Inst Phys Mat, Brno 61662, Czech Republic
[4] Ohio State Univ, Ctr Electron Microscopy & Anal, Columbus, OH 43212 USA
来源：
MATERIALS LETTERS | 2022年 / 308卷
关键词：
Hydrogen embrittlement; Dynamic strain aging; Characterisation; Low-alloy steel; ENVIRONMENTAL DEGRADATION; TEMPERATURE; DEPENDENCE;
D O I：
10.1016/j.matlet.2021.131269
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Fracture mechanics tests in hydrogenated high-temperature water at 288 degrees C on low-alloy reactor pressure vessel steel with high dynamic strain aging (DSA) susceptibility revealed reduced fracture resistance, accelerated crack growth and increased quasi-cleavage appearance than test in high-temperature air. Hydrogen-induced softening by HESIV and HELP concur in synergy with DSA at 288 degrees C, which was evidenced by crack-tip microstructural characterisations.
引用
收藏
页数：5
相关论文
共 50 条
  • [31] Strain-amplitude dependent fatigue resistance of low-alloy pressure vessel steels in high-temperature water
    Wu, XQ
    Katada, Y
    JOURNAL OF MATERIALS SCIENCE, 2005, 40 (08) : 1953 - 1958
  • [32] Effect of long-term thermal aging on magnetic hysteresis for low-alloy pressure vessel steel
    Kobayashi, Satoru
    Gillemot, Ferenc
    Horvath, Akos
    Horvath, Marta
    Laszlo, Almasy
    8TH JOINT EUROPEAN MAGNETIC SYMPOSIA (JEMS2016), 2017, 903
  • [33] Hydrogen-induced embrittlement wear of a high-strength, low-alloy steel in an acidic environment
    Zhang, TC
    Jiang, XX
    Li, SZ
    CORROSION, 1997, 53 (03) : 200 - 205
  • [34] IRRADIATION EMBRITTLEMENT OF A LOW-ALLOY STEEL INTERPRETED IN TERMS OF A LOCAL APPROACH OF CLEAVAGE FRACTURE
    ALMUNDHERI, M
    SOULAT, P
    PINEAU, A
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1989, 12 (01) : 19 - 30
  • [35] Irradiation embrittlement of reactor pressure vessel steel at very high neutron fluence
    Kryukov, A.
    Debarberis, L.
    von Estorff, U.
    Gillemot, F.
    Oszvald, F.
    JOURNAL OF NUCLEAR MATERIALS, 2012, 422 (1-3) : 173 - 177
  • [36] Influence of dynamic strain ageing on fracture behaviour and stretch zone formation of a reactor pressure vessel steel
    Das, Avik R.
    Chowdhury, Tamshuk
    Sivaprasad, S.
    Bar, H. N.
    Narasaiah, N.
    Tarafder, S.
    INTERNATIONAL JOURNAL OF FRACTURE, 2016, 202 (01) : 79 - 91
  • [37] Influence of dynamic strain ageing on fracture behaviour and stretch zone formation of a reactor pressure vessel steel
    Avik R. Das
    Tamshuk Chowdhury
    S. Sivaprasad
    H. N. Bar
    N. Narasaiah
    S. Tarafder
    International Journal of Fracture, 2016, 202 : 79 - 91
  • [38] Hydrogen Embrittlement of a T95 Low-Alloy Steel Charged by Electrochemical Method
    Paterlini, Luca
    Vergani, Laura
    Ormellese, Marco
    Curia, Arianna
    Re, Giorgio
    Bolzoni, Fabio
    MATERIALS, 2025, 18 (05)
  • [39] EFFECTS OF LATTICE STRAINS ON HYDROGEN EMBRITTLEMENT OF A QUENCH-AND-TEMPERED LOW-ALLOY STEEL
    SAKAKI, T
    NAKAMURA, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1974, 14 (03) : 195 - 201
  • [40] Fracture in ferritic reactor steel—dynamic strain aging and cyclic loading
    K. Linga Murty
    Chang-Sung Seok
    JOM, 2001, 53 : 23 - 26
12345