The effect of nickel on sulphidation resistance of austenitic heat resistant alloys

被引：0
|
作者：
Karaminezhaad, M [1 ]
Bateni, MR [1 ]
Kordzadeh, E [1 ]
Moeini, A [1 ]
机构：
[1] Shahidbahonar Univ, Met Grp, Kerman, Iran
来源：
Aerospace Materials and Manufacturing: Development, Testing, and Life Cycle Issues - Honoring William Wallace | 2004年
关键词：
D O I：
暂无
中图分类号：
V [航空、航天];
学科分类号：
08 ; 0825 ;
摘要：
A series of austenitic heat resistant Fe-Ni-Cr-Al alloys with different nickel contents have been investigated at 1100 degrees C and 25, 50, 50,100 hours in S/O bearing atmospheres. Before sulphidation test, the specimens were annealed in argon at 1250 degrees C for 8 hrs. Weight changes were measured using an automatic then-no gravimetric analyzer and corrosion products were analyzed by scanning electro microscope (SEM), energy dispersive X-ray spectrometry (EDAX), X-ray diffraction and optical microscope. The results showed that sulphidation resistance decreased with increasing nickel content. Internal sulphidation controlled by gaseous transport through cracks and pores and the formation of internal sulphide increased when liquid sulphides formed on the surface.
引用
收藏
页码：65 / 75
页数：11
相关论文
共 50 条
  • [31] HEAT-RESISTANCE OF NICKEL-BASE ALLOYS
    RYABTSEV, LA
    IGNATOV, DV
    PRYAKHIN.LI
    RUSSIAN METALLURGY-METALLY-USSR, 1970, (06): : 120 - &
  • [32] Corrosion- and Hydrogen-Resistance of Heat-Resistant Blade Nickel-Cobalt Alloys
    A. I. Balyts’kyi
    Yu. H. Kvasnyts’ka
    L. M. Ivas’kevich
    H. P. Myal’nitsa
    Materials Science, 2018, 54 : 230 - 239
  • [33] Corrosion- and Hydrogen-Resistance of Heat-Resistant Blade Nickel-Cobalt Alloys
    Balyts'kyi, A. I.
    Kvasnyts'ka, Yu. H.
    Ivas'kevich, L. M.
    Myal'nitsa, H. P.
    MATERIALS SCIENCE, 2018, 54 (02) : 230 - 239
  • [34] Effect of conditions of directional solidification and heat treatment on the porosity of single crystals of heat-resistant nickel alloys
    Toloraiya, V.N.
    Zuev, A.G.
    Svetlov, I.L.
    Izvestiya AN SSSR: Metally, 1991, (05): : 70 - 76
  • [35] Protective coatings on nickel heat-resistant alloys (Review)
    Podchernyaeva, I.A.
    Panasyuk, A.D.
    Teplenko, M.A.
    Podol'skij, V.I.
    Poroshkovaya Metallurgiya, 2000, (9-10): : 12 - 27
  • [36] DENDRITIC SEGREGATION IN HEAT-RESISTANT NICKEL ALLOYS.
    Kuleshova, E.A.
    Cherkasova, E.R.
    Logunov, A.V.
    Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka Metallov), 1981, 23 (5-6): : 392 - 396
  • [37] Protective Coatings on Heat-Resistant Nickel Alloys (Review)
    Irina A. Podchernyaeva
    Alla D. Panasyuk
    Powder Metallurgy and Metal Ceramics, 2000, 39 : 434 - 444
  • [38] CARBIDE PHASES IN HEAT-RESISTANT NICKEL-ALLOYS
    PIGROVA, GD
    LEVIN, YY
    PHYSICS OF METALS AND METALLOGRAPHY, 1972, 33 (06): : 166 - 170
  • [39] Modifying castable heat-resistant nickel alloys with zirconium
    Lysenko, NA
    Kudin, VV
    Dolgov, BV
    Tsivirko, EI
    METAL SCIENCE AND HEAT TREATMENT, 1998, 40 (3-4) : 103 - 106
  • [40] MAGNETOSTRICTION OF HEAT-RESISTANT NICKEL-BASE ALLOYS
    KARASYUK, NP
    MIROSHNICHENKO, FD
    GAITOTA, GI
    FIZIKA METALLOV I METALLOVEDENIE, 1973, 36 (04): : 887 - 890
12345