Analysis on Fatigue of Natural Corrosion Steel Bars

被引：1
|
作者：
Li, Shibin [1 ,2 ]
Zhang, Weiping [2 ]
Gu, Xianglin [2 ]
Zhu, Cimian [2 ]
机构：
[1] Shandong Jianzhu Univ, Sch Civil Engn, Jinan 250101, Peoples R China
[2] Tongji Univ, Dept Bldg Engn, Shanghai 200092, Peoples R China
来源：
ADVANCES IN STRUCTURES, PTS 1-5 | 2011年 / 163-167卷
基金：
中国国家自然科学基金;
关键词：
Natural Corrosion; Steel Bar; Test; Fatigue Life; Analysis; REINFORCEMENT;
D O I：
10.4028/www.scientific.net/AMR.163-167.3237
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
To reasonablely assess the residual fatigue life of aged existing reinforced concrete(RC) bridges, axial tensile fatigue tests were conducted on fifteen naturally carbonation-induced corrosion steel bars. The fatigue test results indicate that the existence of corrosion pits reduces the fatigue life of steel bars significantly under the same fagitue stress; with the development of corrosion, the fatigue life of steel bars decays according to negative power exponent law approximately and the attenuation rate increases with stress level augment. The fatigue deterioration law of natural corrosion steel bars is similar to that of accelerated corrosion steel bars, but the attenuation rate is different from that of accelerated corrosion steel bars, and also the influence of stress level on the attenuation rate is just cross to that of accelerated corrosion steel bars. For the complexity of fatigue and corrosion, further Pertinent conclusions remain to be confirmed.
引用
收藏
页码：3237 / 3241
页数：5
相关论文
共 50 条
  • [21] Effects of Corrosion and Ribs on Low Cycle Fatigue Behavior of Reinforcing Steel Bars S400
    Ch. Alk. Apostolopoulos
    V. P. Pasialis
    [J]. Journal of Materials Engineering and Performance, 2010, 19 : 385 - 394
  • [22] CORROSION FATIGUE OF CLAD STEEL
    LEVCHENKO, VA
    KUZYUKOV, AN
    [J]. SOVIET MATERIALS SCIENCE, 1991, 27 (02): : 210 - 212
  • [23] CORROSION FATIGUE OF AN HSLA STEEL
    AHN, SH
    LAWRENCE, FV
    METZGER, MM
    [J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1992, 15 (07) : 625 - 642
  • [24] Corrosion of reinforced steel bars embedded in concrete:: A study of electrochemical and surface analysis
    Bartolo-Pérez, P
    Peña, JL
    Salas, FH
    Wheat, HG
    Hernández-Duque, G
    [J]. CORROSION REVIEWS, 2000, 18 (2-3) : 255 - 266
  • [25] Fatigue flexural analysis of concrete beams reinforced with hybrid GFRP and steel bars
    Xu, Jiajing
    Zhu, Peng
    Ma, Zhongguo John
    Qu, Wenjun
    [J]. ENGINEERING STRUCTURES, 2019, 199
  • [26] Effects of Corrosion and Ribs on Low Cycle Fatigue Behavior of Reinforcing Steel Bars S400
    Apostolopoulos, Ch. Alk.
    Pasialis, V. P.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2010, 19 (03) : 385 - 394
  • [27] SCALE EFFECT IN FATIGUE AND CORROSION FATIGUE OF STEEL
    KARPENKO, GV
    POGORETS.RG
    [J]. DOKLADY AKADEMII NAUK SSSR, 1972, 206 (06): : 1337 - &
  • [28] Electrochemical characteristic analysis of corrosion of coated steel bars in magnesium oxychloride concrete
    Wen, Shao-yong
    Qiao, Hong-xia
    Wang, Peng-hui
    Yang, Tian-xia
    Yang, Zhen-qing
    [J]. EMERGING MATERIALS RESEARCH, 2019, 8 (04) : 696 - 703
  • [29] RANDOM FATIGUE ANALYSIS OF STRUCTURAL STEEL BARS SUBJECTED TO PLASTIC BENDING.
    Goto, Hisao
    Kameda, Hiroyuki
    Koike, Takeshi
    [J]. Memoirs of the Faculty of Engineering, Kyoto University, 1977, 39 (pt 2): : 270 - 284
  • [30] Corrosion fatigue life simulation and reliability analysis of steel structures
    Liu, Heng
    Zong, Liang
    Shao, Yongbo
    Ding, Yang
    [J]. Journal of Constructional Steel Research, 2024, 223
12345