Impermeability of Y3Al5O12 ceramic against molten glassy calcium-magnesium-alumina-silicate

被引：15
|
作者：
Xue, Zhaolu
Ma, Yue
Gong, Shengkai
Guo, Hongbo [1 ]
机构：
[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
来源：
CHINESE JOURNAL OF AERONAUTICS | 2018年 / 31卷 / 12期
基金：
中国国家自然科学基金;
关键词：
Calcium-magnesium-alumina-silicate (CMAS); Ceramics; Thermal barrier coating; Yttrium aluminum garnet; Zirconia; THERMAL BARRIER COATINGS; HIGH-TEMPERATURE ATTACK; PHASE-STABILITY; CONDUCTIVITY; RESISTANCE;
D O I：
10.1016/j.cja.2018.02.007
中图分类号：
V [航空、航天];
学科分类号：
08 ; 0825 ;
摘要：
Degradation of thermal barrier coatings (TBCs) caused by calcium-magnesium-aluminasilica (CMAS) glassy penetration is becoming an urgent issue for TBCs industrial applications. In this work, yttrium aluminum garnet (Y3Al5O12, YAG) nano-powders were synthesized through a chemical co-precipitation route. The resistance of YAG ceramic to glassy CMAS infiltration at 1250 degrees C was evaluated. YAG ceramic bulk sintered at 1700 degrees C for 10 h was comprised of a single garnet-type Y3Al5O12 phase. The molten CMAS glass was suppressed on the surface of the YAG ceramic at 1250 degrees C. A chemical reaction between YAG and the molten CMAS glass did not occur at 1250 degrees C for 24 h, suggesting that YAG could act as an impermeable material against glassy CMAS deposits in the TBC field. (C) 2018 Chinese Society of Aeronautics and Astronautics. Production and hosting by Elsevier Ltd.
引用
收藏
页码：2306 / 2311
页数：6
相关论文
共 50 条
  • [21] Making and spectra property of the composite Yb:Y3Al5O12/ Y3Al5O12 crystal
    Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800, China
    不详
    不详
    Guangxue Xuebao, 2008, 2 (316-320): : 316 - 320
  • [22] Thermodynamics of glass formation and metastable solidification of molten Y3Al5O12
    Lin, IC
    Navrotsky, A
    Weber, JKR
    Nordine, PC
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 1999, 243 (2-3) : 273 - 276
  • [23] High-power Nd:Y3Al5O12 ceramic laser
    Institute for Laser Science, University of Electro-Communications, 1-5-1 Chofugaoka, Chofu, Tokyo 182-8585, Japan
    不详
    不详
    Japanese journal of applied physics, 2000, 39 (10 B)
  • [24] High-power Nd:Y3Al5O12 ceramic laser
    Lu, JR
    Song, J
    Prabhu, M
    Xu, JQ
    Ueda, K
    Yagi, H
    Yanagitani, T
    Kudryashov, A
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 2000, 39 (10B): : L1048 - L1050
  • [25] 110 W ceramic Nd3+ : Y3Al5O12 laser
    J. Lu
    H. Yagi
    K. Takaichi
    T. Uematsu
    J.-F. Bisson
    Y. Feng
    A. Shirakawa
    K.-I. Ueda
    T. Yanagitani
    A.A. Kaminskii
    Applied Physics B, 2004, 79 : 25 - 28
  • [26] Efficient Yb3+:Y3Al5O12 ceramic microchip lasers
    Dong, Jun
    Shirakawa, Akira
    Ueda, Ken-ichi
    Yagi, Hideki
    Yanagitani, Takagimi
    Kaminskii, Alexander A.
    APPLIED PHYSICS LETTERS, 2006, 89 (09)
  • [27] 110 W ceramic Nd3+ : Y3Al5O12 laser
    Lu, J
    Yagi, H
    Takaichi, K
    Uematsu, T
    Bisson, JF
    Feng, Y
    Shirakawa, A
    Ueda, KI
    Yanagitani, T
    Kaminskii, AA
    APPLIED PHYSICS B-LASERS AND OPTICS, 2004, 79 (01): : 25 - 28
  • [28] INACTIVE ABSORPTION IN Y3AL5O12
    GORBAN, IS
    GUMENYUK, AF
    DEGODA, VY
    OPTIKA I SPEKTROSKOPIYA, 1985, 58 (03): : 705 - 707
  • [29] HYDROTHERMAL GROWTH OF Y3AL5O12
    PUTTBACH, RC
    MONCHAMP, RR
    NIELSEN, JW
    JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1967, S : 569 - &
  • [30] Mechanisms of nonstoichiometry in Y3Al5O12
    Patel, A. P.
    Levy, M. R.
    Grimes, R. W.
    Gaume, R. M.
    Feigelson, R. S.
    McClellan, K. J.
    Stanek, C. R.
    APPLIED PHYSICS LETTERS, 2008, 93 (19)
12345